Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6T C240K MITSUI CHEM JAPAN
ARLEN™
Electrical field、Electronic field
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | MITSUI CHEM JAPAN/C240K |
|---|---|---|---|
| Glass Fiber Content | 40 % |
| Basic performance | Test Condition | Test Method | MITSUI CHEM JAPAN/C240K |
|---|---|---|---|
| Water absorption rate | 23℃,24小时在水里(2mmt,100℃) | ASTM D-570 | 0.2(2.8) % |
| Mechanical properties | Test Condition | Test Method | MITSUI CHEM JAPAN/C240K |
|---|---|---|---|
| elongation | dry(moist) | ASTM D-638 | 3(3) % |
| Flexural modulus | dry(moist) | ASTM D-790 | 13000(9000) Mpa |
| Rockwell hardness | ASTM D-785 | 110 M Scale | |
| tensile strength | dry(moist) | ASTM D-638 | 210(180) Mpa |
| bending strength | dry(moist) | ASTM D-790 | 300(260) Mpa |
| Impact strength of cantilever beam gap | dry(moist) | ASTM D-256 | 85(90) J/m |
| Electrical performance | Test Condition | Test Method | MITSUI CHEM JAPAN/C240K |
|---|---|---|---|
| dielectric strength | dry | ASTM D-149 | 30 KV/mm |
| Dissipation Factor | 10 | ASTM D-150 | 0.018 |
| Volume resistivity | dry | ASTM D-257 | 10 Ω.cm |
| dielectric constant | 10 | ASTM D-150 | 4.5 |
| physical property | Test Condition | Test Method | MITSUI CHEM JAPAN/C240K |
|---|---|---|---|
| Shrinkage rate | 2mmt | ASTM D-955 | 0.4(0.8) % |
| Thermal performance | Test Condition | Test Method | MITSUI CHEM JAPAN/C240K |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D-648 | 300 °C |
| melting temperature | 310 °C | ||
| Linear coefficient of thermal expansion | ASTM D-696 | 2.0(4.5) | |
| Glass transition temperature (Tg) | 85 °C | ||
| UL flame retardant rating | UL 94 | HB |