PBT NH-2306F LG CHEM KOREA
LUPOX®
Electronic field,Electrical field,Electrical/Electronic Applications
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/NH-2306F |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 59 J/m |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/NH-2306F |
|---|---|---|---|
| tensile strength | Break,3.20mm | ASTM D638 | 98.1 Mpa |
| elongation | 断裂,3.20mm | ASTM D638 | 2.0 % |
| Flexural modulus | 3.20mm | ASTM D790 | 8830 Mpa |
| bending strength | 屈服,3.20mm | ASTM D790 | 162 Mpa |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/NH-2306F |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI)4 | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | LG CHEM KOREA/NH-2306F |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| 0.8mm | UL 94 | V-0 | |
| 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG CHEM KOREA/NH-2306F |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30-1.0 % |
| melt mass-flow rate | 265°C/2.16kg | ASTM D1238 | 7.0 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.070 % |
| density | ASTM D792 | 1.57 g/cm³ |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/NH-2306F |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 210 °C |
| melting temperature | ASTM D3418 | 223 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |