Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO PX9406P-7001 SABIC INNOVATIVE THAILAND
NORYL™
Electronic communication 、Electronic communication 、building materials、Profile
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/PX9406P-7001 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 9.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/PX9406P-7001 |
|---|---|---|---|
| bending strength | --2,3 | ISO 178 | 108 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 73.0 Mpa |
| bending strength | -- | ASTM D790 | 99.0 Mpa |
| Flexural modulus | --2 | ISO 178 | 2600 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 4.5 % |
| Flexural modulus | -- | ASTM D790 | 2350 Mpa |
| tensile strength | 屈服 | 内部方法 | 63.0 Mpa |
| Tensile strain | 断裂 | 内部方法 | 85 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/PX9406P-7001 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+16 ohms | |
| dielectric constant | 60 Hz | ASTM D150 | 2.80 |
| 50 kHz | ASTM D150 | 2.80 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/PX9406P-7001 |
|---|---|---|---|
| UL flame retardant rating | 2.5 mm | UL 94 | 5VA |
| 0.75 mm | UL 94 | V-0 | |
| 0.40 mm | UL 94 | V-2 |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/PX9406P-7001 |
|---|---|---|---|
| melt viscosity | 280°C, 1500 sec^-1 | ISO 11443 | 278 Pa·s |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/PX9406P-7001 |
|---|---|---|---|
| Melt volume flow rate | 280°C/10.0 kg | ISO 1133 | 27.0 cm3/10min |
| 300°C/5.0 kg | ISO 1133 | 23.0 cm3/10min | |
| Water absorption rate | 24 hr | ASTM D570 | 0.070 % |
| melt mass-flow rate | 250°C/10.0 kg | ASTM D1238 | 3.9 g/10 min |
| Melt volume flow rate | 280°C/5.0 kg | ISO 1133 | 10.0 cm3/10min |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/PX9406P-7001 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 142 °C |
| -- | ISO 306/A120 | 151 °C | |
| Linear coefficient of thermal expansion | 流动 : -30 到 30°C | TMA | 7.0E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 7.6E-5 cm/cm/°C | |
| 流动 : -40 到 40°C | ISO 11359-2 | 6.6E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 125 °C |
| 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 136 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距5，HDT | ISO 75-2/Af | 117 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| injection | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/PX9406P-7001 |
|---|---|---|---|
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 275 to 305 °C | ||
| drying temperature | 105 to 110 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 255 to 300 °C | ||
| Temperature at the rear of the barrel | 245 to 295 °C | ||
| Exhaust hole depth | 0.038 to 0.051 mm | ||
| Temperature at the front of the material cylinder | 265 to 305 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 100 °C | ||
| Spray nozzle temperature | 275 to 305 °C |