PC
PC SABIC INNOVATIVE US EXL9134 BK
US$ 3,876 / MT
FOB China Main Port
injectionTest ConditionTest MethodSABIC INNOVATIVE US/EXL9134 BK
Back pressure0.300 to 0.700 Mpa
Temperature at the front of the material cylinder295 to 315 °C
Screw speed40 to 70 rpm
Mold temperature70 to 95 °C
Processing (melt) temperature295 to 315 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Spray nozzle temperature290 to 310 °C
Exhaust hole depth0.025 to 0.076 mm
drying temperature120 °C
Temperature in the middle of the barrel280 to 305 °C
drying time3.0 to 4.0 hr
Temperature at the rear of the barrel270 to 295 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL9134 BK
bending strength--5,6ISO 17887.0 Mpa
Bending modulus50.0 mm Span4ASTM D7902400 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79092.0 Mpa
elongationBreakISO 527-2/50110 %
Yield3ASTM D6386.0 %
YieldISO 527-2/506.0 %
Break3ASTM D638120 %
tensile strengthBreakISO 527-2/5057.0 Mpa
YieldISO 527-2/5056.0 Mpa
Yield3ASTM D63858.0 Mpa
Tensile modulus--2ASTM D6382100 Mpa
--ISO 527-2/12000 Mpa
Bending modulus--5ISO 1782100 Mpa
tensile strengthBreak3ASTM D63859.0 Mpa
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9134 BK
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8316.2E-5 cm/cm/°C
Across Flow : -40°CISO 11359-26.2E-5 cm/cm/°C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af118 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8316.1E-5 cm/cm/°C
Vicat softening temperature--ISO 306/B50139 °C
RTI ElecUL 746125 °C
RTI ImpUL 746115 °C
RTIUL 746120 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648123 °C
Vicat softening temperature--ISO 306/B120141 °C
--ASTM D152510140 °C
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL9134 BK
Hot filament ignition temperature3.0 mmIEC 60695-2-13825 °C
1.5 mmIEC 60695-2-13825 °C
UL flame retardant rating3.0 mmUL 945VA
1.5 mmUL 94V-0
Burning wire flammability index1.5 mmIEC 60695-2-12960 °C
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL9134 BK
Water absorption rateSaturation, 23°CISO 620.40 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113315.0 cm3/10min
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.15 %
Outdoor applicabilityUL 746Cf1
Shrinkage rate3.20 mm，FlowInternal Method0.40 - 0.80 %
melt mass-flow rate300°C/1.2 kgASTM D123816 g/10 min
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9134 BK
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA35 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Dart impact23°C, Total EnergyASTM D376367.0 J
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂