Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PC/PBT 5220U-1001 SABIC INNOVATIVE SHANGHAI

XENOY™

chip,Industrial applications,Lawn equipment,Garden equipment,Household goods,Outdoor applications,Electrical field,Electronic field,Architectural application field,sporting goods,Electrical appliances,lens,Medical supplies,Nursing supplies,Plastic bag,Automotive sector,Lighting applications,Non specific food,Automotive External Parts

Impact modification,Low temperature impact re,Chemical resistance

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-1001
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	84.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span10	ISO 75-2/Af	75.0 °C
		0.45 MPa, Unannealed, 6.40 mm	ASTM D648	107 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0 °C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	9.0E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	9.5E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	9.0E-5 cm/cm/°C
RTI		UL 746	75.0 °C
RTI Elec		UL 746	75.0 °C
RTI Imp		UL 746	75.0 °C
Vicat softening temperature	--	ISO 306/B120	125 °C
		--	ISO 306/B50	120 °C
		--	ASTM D152511	122 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-1001
Bending modulus	--7	ISO 178	2000 Mpa
Bending modulus		50.0 mm Span6	ASTM D790	2030 Mpa
bending strength	--7,8	ISO 178	80.0 Mpa
bending strength		Yield, 50.0 mm Span6	ASTM D790	84.0 Mpa
elongation	Yield	ISO 527-2/50	4.0 %
		Yield5	ASTM D638	4.0 %
		Break5	ASTM D638	120 %
		Break	ISO 527-2/50	120 %
Tensile modulus	--4	ASTM D638	2250 Mpa
		--3	ASTM D638	2250 Mpa
		--	ISO 527-2/1	2050 Mpa
tensile strength	Yield	ISO 527-2/50	50.0 Mpa
		Break	ISO 527-2/50	50.0 Mpa
		Break5	ASTM D638	51.0 Mpa
		Yield5	ASTM D638	53.0 Mpa

Electrical performance	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-1001
Arc resistance	ASTM D495	PLC 5
Compared to the anti leakage trace index	UL 746	PLC 1
High arc combustion index	UL 746	PLC 0
High voltage arc tracing rate	UL 746	PLC 0
Hot wire ignition	UL 746	PLC 3

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-1001
melt mass-flow rate	250°C/5.0 kg	ISO 1133	16 g/10 min
Melt Volume Flow Rate (MVR)	250°C/5.0 kg	ISO 1133	15.0 cm3/10min
Outdoor applicability		UL 746C	f2
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.80 - 1.0 %
Shrinkage rate		Across FlowFlow 2	Internal Method	0.80 - 1.0 %
Specific volume		ASTM D792	0.830 cm³/g
Water absorption rate	Saturation, 23°C	ISO 62	0.50 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.15 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-1001
Dart impact	23°C, Total Energy	ASTM D3763	60.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-1001
UL flame retardant rating	1.5 mm	UL 94	HB

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/5220U-1001
Back pressure			0.300 to 0.700 Mpa
drying temperature			110 °C
drying time			4.0 to 6.0 hr
Exhaust hole depth			0.013 to 0.020 mm
Mold temperature			65 to 90 °C
Processing (melt) temperature			260 to 275 °C
Screw speed			50 to 80 rpm
Spray nozzle temperature			255 to 270 °C
Suggested injection volume			50 to 80 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			255 to 275 °C
Temperature at the rear of the barrel			245 to 265 °C
Temperature in the middle of the barrel			250 to 270 °C

Get App