Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO WCP921-111 SABIC INNOVATIVE SHANGHAI
FLEX NORYL™
Electronic and electrical
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCP921-111
Shore hardness邵氏A,30秒ASTM D224088
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCP921-111
Flexural modulus100mmSpanASTM D790180 Mpa
elongation断裂ASTM D638150 %
Flexural modulusISO 178200 Mpa
tensile strength 断裂ASTM D63815.0 Mpa
Tensile strain断裂ISO 527-2/50140 %
tensile strength 断裂ISO 527-2/5015.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCP921-111
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
Volume resistivityASTM D2577.1E+15 ohms·cm
dielectric strength2.00mm,inOilIEC 60243-125 KV/mm
relative permittivity1MHzIEC 602502.80
Dissipation Factor1MHzIEC 602500.029
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCP921-111
Burning wire flammability index3.0mmIEC 60695-2-12850 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13725 °C
UL flame retardant rating6.0mmUL 94V-0
Limiting Oxygen IndexISO 4589-224 %
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCP921-111
melt mass-flow rate250°C/2.16kgASTM D123817 g/10min
Shrinkage rateMD：24小时ASTM D9550.55 %
Water absorption rate23°C,24hrASTM D5700.060 %
melt mass-flow rate210°C/5.0kgASTM D123815 g/10min
Shrinkage rateTD：24hrASTM D9550.65 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/WCP921-111
brittle temperatureASTM D746<-40.0 °C