PC XANTAR® 24 U Mitsubishi Chemical Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 24 U |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C | ISO 180/4A | 80 kJ/m² |
hardness | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 24 U |
---|---|---|---|
Rockwell hardness | M级 | ISO 2039-2 | 70 |
Mechanical properties | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 24 U |
---|---|---|---|
Nominal tensile fracture strain | ISO 527-2 | >50 % | |
Tensile modulus | ISO 527-2 | 2300 MPa | |
Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
tensile strength | 屈服 | ISO 527-2 | 60.0 MPa |
Flexural modulus | ISO 178 | 2400 MPa | |
bending strength | ISO 178 | 90.0 MPa |
Electrical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 24 U |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
dielectric strength | IEC 60243-1 | 29 kV/mm | |
Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
relative permittivity | 100Hz | IEC 60250 | 3.00 |
Dissipation Factor | 100Hz | IEC 60250 | 6.6E-04 |
relative permittivity | 1MHz | IEC 60250 | 2.90 |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
Dissipation Factor | 1MHz | IEC 60250 | 9.2E-03 |
optical performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 24 U |
---|---|---|---|
transmissivity | ASTM D1003 | 89.0 % |
flammability | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 24 U |
---|---|---|---|
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
UL flame retardant rating | 0.75mm | IEC 60695-11-10,-20 | V-2 |
1.5mm | IEC 60695-11-10,-20 | V-2 | |
Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 800 °C |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 875 °C |
1.5mm | IEC 60695-2-13 | 825 °C | |
Limiting Oxygen Index | ISO 4589-2 | 26 % |
physical property | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 24 U |
---|---|---|---|
Shrinkage rate | MD | ISO 294-4 | 0.60 % |
Water absorption rate | 23°C,24hr | ISO 62 | 0.35 % |
Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 7.00 cm³/10min |
density | ISO 1183 | 1.20 g/cm³ | |
Viscosity value | 降低的粘度 | ISO 1628 | 52.0 ml/g |
Thermal performance | Test Condition | Test Method | Mitsubishi Chemical Corporation/XANTAR® 24 U |
---|---|---|---|
RTI Imp | 0.75mm | UL 746 | 125 °C |
RTI Str | 0.75mm | UL 746 | 125 °C |
thermal conductivity | 0.24 W/m/K | ||
vicat | ISO 306/B50 | 150 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 130 °C |
RTI Str | 3.0mm | UL 746 | 130 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.5E-05 cm/cm/°C |
RTI Elec | 3.0mm | UL 746 | 130 °C |
RTI Imp | 3.0mm | UL 746 | 130 °C |
ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
RTI Elec | 0.75mm | UL 746 | 130 °C |