Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT SK605 BK851 DUPONT KOREA
Crastin®
Electronic and electrical、Automotive Applications、Structural components、Industrial applications、Automotive Applications、Structural components、Industrial applications、Automotive Applications
Glass fiber reinforced、Filler: Glass fiber reinf、30% by weight ratio)、30% filler by weight、Good strength、Good hardness (glass fibe、30% by weight ratio)、30% filler by weight、Good strength、Good hardness (glass fibe
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | DUPONT KOREA/SK605 BK851 |
|---|---|---|---|
| Limiting Oxygen Index | ASTM D2863 | 19 % |
| Impact resistance | Test Condition | Test Method | DUPONT KOREA/SK605 BK851 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 55 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 75 kJ/m² |
| Suspended wall beam without notch impact strength | -40°C | ISO 180/1U | 55 kJ/m² |
| 23°C | ISO 180/1U | 60 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 11 kJ/m² |
| -40°C | ISO 180/1A | 10 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 75 kJ/m² |
| Supplementary Information | Test Condition | Test Method | DUPONT KOREA/SK605 BK851 |
|---|---|---|---|
| Odor | VDA270 | 3.00 | |
| Emissions of Organic Compounds | VDA277 | 140 µgC/g |
| Mechanical properties | Test Condition | Test Method | DUPONT KOREA/SK605 BK851 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10000 Mpa | |
| tensile strength | 23℃ | ASTM D638 | 140 MPa |
| Tensile creep modulus | 1000hr | ISO 899-1 | 6600 Mpa |
| tensile strength | 断裂 | ISO 527-2 | 140 Mpa |
| Impact strength of cantilever beam gap | ASTM D256 | 101 J/m | |
| Suspended wall beam without notch impact strength | 23℃ | ASTM D256 | 998 J/m |
| compressive strength | 5 mm/min, 3.20 mm, 23 ℃ | ASTM D695 | 202 MPa |
| Tensile modulus | 23℃ | ASTM D638 | 10000 MPa |
| Tensile creep modulus | 1hr | ISO 899-1 | 9000 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 112 J/m |
| bending strength | ISO 178 | 200 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.7 % |
| Flexural modulus | ISO 178 | 9000 Mpa | |
| Impact strength of cantilever beam gap | -40℃ | ASTM D256 | 101 J/m |
| elongation at break | 23℃ | ASTM D638 | 2.6 % |
| Flexural modulus | 23℃ | ASTM D790 | 8970 MPa |
| Suspended wall beam without notch impact strength | -40℃ | ASTM D256 | 1120 J/m |
| Electrical performance | Test Condition | Test Method | DUPONT KOREA/SK605 BK851 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| dielectric strength | IEC 60243-1 | 38 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.90 |
| Dissipation Factor | 100Hz | IEC 60250 | 7.5E-04 |
| relative permittivity | 1MHz | IEC 60250 | 3.80 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.018 |
| flammability | Test Condition | Test Method | DUPONT KOREA/SK605 BK851 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| atomization | refraction，F值 | ISO 6452 | 99 % |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 19 % | |
| burning rate | 1.00mm | ISO 3795 | 41 mm/min |
| physical property | Test Condition | Test Method | DUPONT KOREA/SK605 BK851 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.35 % |
| density | ASTM D792 | 1.53 | |
| ISO 1183 | 1.53 g/cm³ | ||
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 7.00 cm3/10min |
| SpecificHeatCapacity of Melt | 1730 J/kg/°C | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % |
| Shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.30 % | |
| viscosity number | ISO 307 | 100 cm³/g | |
| melt mass-flow rate | ISO 1133 | 10 g/10min | |
| MediumDensity | 1.36 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| ThermalConductivityofMelt | 0.28 W/m/K |
| Thermal performance | Test Condition | Test Method | DUPONT KOREA/SK605 BK851 |
|---|---|---|---|
| UL flame retardant rating | 3.00 mm | UL 94 | HB |
| vicat | ISO 306/B50 | 215 °C | |
| Linear coefficient of thermal expansion | 平行流动方向，73 to 130°F (23 to 55℃) | ASTM E831 | 0.000030 cm/cm/℃ |
| 垂直流动方向，73 to 130°F (23 to 55℃) | ASTM E831 | 0.000090 cm/cm/℃ | |
| Heat distortion temperature | 0.45Mpa,未退火，HDT | ASTM D648 | 220 ℃ |
| melting temperature | ISO 11357-3 | 224 °C | |
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3E-05 cm/cm/°C |
| UL flame retardant rating | 1.50 mm | UL 94 | HB |
| Heat distortion temperature | 1.8Mpa,未退火，HDT | ASTM D648 | 205 ℃ |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 9E-05 cm/cm/°C |