Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP RIPP 490 A SCHULMAN USA
POLYFORT®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | A SCHULMAN USA/RIPP 490 |
|---|---|---|---|
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 65.0 °C |
| RTIElec | 1.5mm | UL746 | 65.0 °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 72.0 °C |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Evolution Calendar intelligent importer | 3.0mm | UL746 | 65.0 °C |
| RTIStr | 1.5mm | UL746 | 65.0 °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 150 °C |
| RTIElec | 3.0mm | UL746 | 65.0 °C |
| RTIStr | 3.0mm | UL746 | 65.0 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/Af | 58.0 °C |
| 0.45MPa,未退火 | ISO75-2/Bf | 108 °C |
| Physical | Test Condition | Test Method | A SCHULMAN USA/RIPP 490 |
|---|---|---|---|
| Melt Volume flow Rate | 230°C/2.16kg | ISO1133 | 9.00 cm3/10min |
| Mechanical Properties | Test Condition | Test Method | A SCHULMAN USA/RIPP 490 |
|---|---|---|---|
| Tensile Stress | 屈服 | ISO527-2/1A/50 | 22.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/1A/50 | 3.0 % |
| Tensile Modulus | ISO527-2/1A/1 | 1900 Mpa |
| Other | Test Condition | Test Method | A SCHULMAN USA/RIPP 490 |
|---|---|---|---|
| Remarks | 注射成型 | ||
| characteristic | 磷含量，低（到无），共聚物，阻燃性能 |
| Physical Properties | Test Condition | Test Method | A SCHULMAN USA/RIPP 490 |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.04 |
| Impact Properties | Test Condition | Test Method | A SCHULMAN USA/RIPP 490 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 37 kJ/m² |
| -30°C | ISO179/1eU | 11 kJ/m² |
| Flammability | Test Condition | Test Method | A SCHULMAN USA/RIPP 490 |
|---|---|---|---|
| Burning Rate | 3.00mm,自动灭火 | ISO3795 | 0.0 mm/min |
| 1.50mm,自动灭火 | ISO3795 | 0.0 mm/min | |
| Flame Rating | 3.0mm | IEC60695-11-10,-20 | V-0 |
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 725 °C |
| Flame Rating | 3.0mm | UL94 | V-0 |
| Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 960 °C |
| Oxygen Index | ISO4589-2 | 36 % | |
| Flame Rating | 1.5mm | UL94 | V-0 |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 °C |
| Flame Rating | 1.5mm | IEC60695-11-10,-20 | V-0 |
| Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 725 °C |
| Electrical Properties | Test Condition | Test Method | A SCHULMAN USA/RIPP 490 |
|---|---|---|---|
| High Amp Arc Ignition | 1.5mm | UL746 | PLC 0 |
| 3.0mm | UL746 | PLC 0 | |
| Hot-wire Ignition | 3.0mm | UL746 | PLC 0 |
| 1.5mm | UL746 | PLC 3 | |
| Volume Resistivity | IEC60093 | >1.0E+13 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 600 V | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms |