Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3K BASF SHANGHAI
Ultramid®
Electrical field、Electronic field、Industrial machinery、Industrial applications、Electronic insulation、Electronic insulation
High mobility、Oil resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF SHANGHAI/A3K |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.0 kJ/m² |
| Basic performance | Test Condition | Test Method | BASF SHANGHAI/A3K |
|---|---|---|---|
| density | ISO 1183 | 1130 Kg/m | |
| Water absorption rate | Saturation | ISO 62 | 8.5 % |
| Equilibrium | ISO 62 | 2.8 % |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/A3K |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eA | 5 KJ/m |
| Tensile modulus | ISO 527-2 | 3600 MPa | |
| tensile strength | Yield | ISO 527-2 | 87 MPa |
| 屈服,23°C | ISO 527-2 | 87.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.2 % |
| Tensile modulus | 23°C | ISO 527-2 | 3600 Mpa |
| Tensile strain | Yield | ISO 527-2 | 4.2 % |
| physical property | Test Condition | Test Method | BASF SHANGHAI/A3K |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.8 % |
| 饱和,23°C | ISO 62 | 8.5 % | |
| density | ISO 1183 | 1.13 g/cm³ |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/A3K |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 200 °C |
| melting temperature | DSC | ISO 3146 | 260 ℃ |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C |
| 1.8MPa，HDT | ISO 75-2 | 75 ℃ | |
| melting temperature | ISO 3146 | 260 °C |