Product Name / Manufacturer / Model

Grade

Reference Price

PC/ABS SABIC INNOVATIVE NANSHA CX7240U-701

Injection grade

US$ 4,770 / MT

FOB Guangzhou port, China

injection	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Back pressure			0.300 to 0.700 Mpa
Temperature at the front of the material cylinder			265 to 300 °C
Screw speed			40 to 70 rpm
Mold temperature			60 to 90 °C
Processing (melt) temperature			270 to 300 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.040 %
Spray nozzle temperature			265 to 300 °C
Exhaust hole depth			0.038 to 0.076 mm
drying temperature			90 °C
Temperature in the middle of the barrel			260 to 300 °C
drying time			4.0 hr
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			260 to 300 °C
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
bending strength	--5,6	ISO 178	96.0 Mpa
Bending modulus	50.0 mm Span4	ASTM D790	2750 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	104 Mpa
elongation	Break	ISO 527-2/50	90 %
		Yield3	ASTM D638	4.1 %
		Yield	ISO 527-2/50	4.0 %
		Break3	ASTM D638	100 %
tensile strength	Break	ISO 527-2/50	50.0 Mpa
		Yield3	ASTM D638	65.0 Mpa
		Yield	ISO 527-2/50	65.0 Mpa
Tensile modulus	--2	ASTM D638	2950 Mpa
Tensile modulus		--	ISO 527-2/1	2530 Mpa
Bending modulus	--5	ISO 178	2500 Mpa
tensile strength	Break3	ASTM D638	58.0 Mpa
flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
UL flame retardant rating	0.40 mm	UL 94	V-2
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800 °C
UL flame retardant rating	3.0 mm	UL 94	5VA
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	825 °C
UL flame retardant rating	0.75 mm	UL 94	V-0
		0.60 mm	UL 94	V-1
		1.5 mm	UL 94	5VB
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	5.4E-5 cm/cm/°C
		Across Flow : -40°C	ISO 11359-2	5.4E-5 cm/cm/°C
		Flow : -40 to 40°C	ISO 11359-2	6.2E-5 cm/cm/°C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	93.0 °C
Hot deformation temperature		0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.3E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	110 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0 °C
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
RTI		UL 746	90.0 °C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0 °C
Vicat softening temperature	--	ISO 306/B120	113 °C
Vicat softening temperature		--	ASTM D152510	106 °C
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Compared to the anti leakage trace index		UL 746	PLC 3
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0 cm3/10min
Water absorption rate	Saturation, 23°C	ISO 62	0.20 %
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	16 g/10 min
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10 %
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.60 %
impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	65.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²

Supplier Join