PC/ABS CX7240U-701 SABIC INNOVATIVE NANSHA

CYCOLOY™

Electrical field,Electronic field,Architectural application field,Outdoor applications,Engine hood parts,Medical supplies,Nursing supplies,Plastic bag,Casters,Aerospace Applications,Liquid handling

Flame retardant,High impact resistance,High mobility,Developing shock resistan

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	100 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	89.0 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	93.0 °C
		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	99.0 °C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	5.4E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	6.3E-5 cm/cm/°C
		Flow : -40 to 40°C	ISO 11359-2	6.2E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	5.4E-5 cm/cm/°C
RTI		UL 746	90.0 °C
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
Vicat softening temperature	--	ISO 306/B120	113 °C
		--	ISO 306/B50	110 °C
		--	ASTM D152510	106 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Bending modulus	--5	ISO 178	2500 Mpa
Bending modulus		50.0 mm Span4	ASTM D790	2750 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	104 Mpa
bending strength		--5,6	ISO 178	96.0 Mpa
elongation	Yield	ISO 527-2/50	4.0 %
		Yield3	ASTM D638	4.1 %
		Break3	ASTM D638	100 %
		Break	ISO 527-2/50	90 %
Tensile modulus	--2	ASTM D638	2950 Mpa
Tensile modulus		--	ISO 527-2/1	2530 Mpa
tensile strength	Yield	ISO 527-2/50	65.0 Mpa
		Break	ISO 527-2/50	50.0 Mpa
		Break3	ASTM D638	58.0 Mpa
		Yield3	ASTM D638	65.0 Mpa

Electrical performance	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Compared to the anti leakage trace index	UL 746	PLC 3
High arc combustion index	UL 746	PLC 0
Hot wire ignition	UL 746	PLC 3

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
melt mass-flow rate	260°C/2.16 kg	ASTM D1238	16 g/10 min
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	15.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.20 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.10 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Charpy Notched Impact Strength	23°C	ISO 179/1eA	20 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	10 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	65.0 J

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Burning wire flammability index	0.75 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800 °C
Hot filament ignition temperature		1.0 mm	IEC 60695-2-13	825 °C
UL flame retardant rating	3.0 mm	UL 94	5VA
		0.60 mm	UL 94	V-1
		0.75 mm	UL 94	V-0
		0.40 mm	UL 94	V-2
		1.5 mm	UL 94	5VB

injection	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CX7240U-701
Back pressure			0.300 to 0.700 Mpa
drying temperature			90 °C
drying time			4.0 hr
Exhaust hole depth			0.038 to 0.076 mm
Hopper temperature			60 to 80 °C
Mold temperature			60 to 90 °C
Processing (melt) temperature			270 to 300 °C
Screw speed			40 to 70 rpm
Spray nozzle temperature			265 to 300 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.040 %
Temperature at the front of the material cylinder			265 to 300 °C
Temperature at the rear of the barrel			260 to 300 °C
Temperature in the middle of the barrel			260 to 300 °C