TPO MT61BS-BK GS KOREA
--
Automotive interior equip
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | GS KOREA/MT61BS-BK |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 90 |
| Supplementary Information | Test Condition | Test Method | GS KOREA/MT61BS-BK |
|---|---|---|---|
| process temperature | 210to230 °C | ||
| Emission | VDA277 | <5.0E-5 g | |
| Odor | 80°C | 2.80 |
| Mechanical properties | Test Condition | Test Method | GS KOREA/MT61BS-BK |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 190 % |
| Flexural modulus | ASTM D542 | 1860 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 27.5 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2000 Mpa |
| scratch resistance | DeltaL | 0.800 |
| flammability | Test Condition | Test Method | GS KOREA/MT61BS-BK |
|---|---|---|---|
| atomization | 100°C | DIN 75201 | <2.0 mg |
| physical property | Test Condition | Test Method | GS KOREA/MT61BS-BK |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.1 % |
| MD | ASTM D955 | 1.3 % | |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 27 g/10min |
| Shrinkage rate | TD | 内部方法 | 1.1 % |
| TD | ASTM D955 | 1.3 % | |
| melt mass-flow rate | ASTM D1238 | 27 g/10min | |
| Volatile compounds | 内部方法 | 0.10 % | |
| ash content | 600°C | 内部方法 | 16 % |
| Thermal performance | Test Condition | Test Method | GS KOREA/MT61BS-BK |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 137 °C |