Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LGK3020-739 SABIC INNOVATIVE JAPAN
LEXAN™
Electronic and electrical、Home appliance accessorie、Automotive components
High temperature resistan、Flame retardant、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK3020-739 |
|---|---|---|---|
| dielectric strength | 3.20mm,inOil | ASTM D149 | 18 KV/mm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK3020-739 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 4.0 % |
| tensile strength | 断裂 | ASTM D638 | 118 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 6580 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 148 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK3020-739 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK3020-739 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.13 % |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.050-0.25 % |
| TD:3.20mm | 内部方法 | 0.15-0.35 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/LGK3020-739 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 146 °C |
| Linear coefficient of thermal expansion | MD:-30到30°C | ASTM D696 | 2.7E-05 cm/cm/°C |
| TD:-30到30°C | ASTM D696 | 4.7E-05 cm/cm/°C |