Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BGZ-15/2 BK EMS-CHEMIE SWITZERLAND
Grilon®
Home appliance components、Automotive interior parts、Electrical applications
Glass fiber reinforced、High impact resistance、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | kJ/m² | 11 12 |
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 75 90 |
| -30°C | kJ/m² | 70 75 | |
| Charpy Notched Impact Strength | 23°C | kJ/m² | 20 25 |
| Mechanical properties | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 BK |
|---|---|---|---|
| Tensile modulus | MPa | 5300 2800 | |
| Tensile stress | 断裂 | MPa | 110 65.0 |
| Tensile strain | 断裂 | % | 5.0 15 |
| Electrical performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 BK |
|---|---|---|---|
| Surface Resistivity | ohms | -- 1E+12 | |
| Volume resistivity | ohms·cm | 1E+14 1E+13 | |
| dielectric strength | kV/mm | 40 35 | |
| CTI | V | -- 600 |
| flammability | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 BK |
|---|---|---|---|
| Flammability level | 0.8mm | HB -- |
| physical property | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 BK |
|---|---|---|---|
| Shrinkage rate | MD | % | 0.20 -- |
| density | g/cm³ | 1.18 -- | |
| Water absorption rate | 饱和,23°C | % | 8.0 -- |
| Shrinkage rate | TD | % | 0.70 -- |
| Water absorption rate | 平衡,23°C,50%RH | % | 2.0 -- |
| Thermal performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 BK |
|---|---|---|---|
| Continuous use temperature | --3 | °C | 90.0到120 -- |
| MD | cm/cm/°C | 5E-05 -- | |
| 1.8MPa,未退火 | °C | 190 -- | |
| TD | cm/cm/°C | 1.2E-04 -- | |
| 8.0MPa,未退火 | °C | 55.0 -- | |
| Continuous use temperature | --4 | °C | 160 -- |
| Melting temperature 5 | °C | 222 -- |