PPS 3130A1 JAPAN POLYPLASTIC

DURAFIDE®

Fitness equipment,sporting goods

High impact resistance,Glass fiber reinforced

UL

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

Supplementary Information	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
ColourNumber			HF2000/HD9100

hardness	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
Rockwell hardness	M-Scale	ISO 2039-2	100

Basic Performance	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
density		ISO 1183	1.62
Melt viscosity	310℃,1000/sec	ISO 11443	200 Pa·s
Water absorption rate	23℃,水中24hr	ISO 62	0.02 %

thermal performance	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
Hot deformation temperature	1.8MPa	ISO 75-1	210 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	210 °C
Linear coefficient of thermal expansion	TD	Internal Method	4E-05 cm/cm/°C
		Across Flow		4
		Flow	ISO 11359-2	2
		MD	Internal Method	2E-05 cm/cm/°C
			ASTM D696/ISO 11359	2 mm/mm.℃
Melting temperature			210 ℃（℉）

mechanical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
Bending modulus		ISO 178	11500 Mpa
Bending modulus			ASTM D790/ISO 178	11.500 kg/cm²(MPa)[Lb/in²]
bending strength		ISO 178	230 Mpa
Charpy Notched Impact Strength		ISO 179/1eA	2.5 KJ/m
Elongation at Break		ASTM D638/ISO 527	1.7 %
Fracture strain		ISO 527-1	1.7 %
Tensile modulus		ASTM D638/ISO 527	230 kg/cm²(MPa)[Lb/in²]
Tensile strain	Break	ISO 527-2	1.7 %
tensile strength		ASTM D638/ISO 527	125 kg/cm²(MPa)[Lb/in²]
			ISO 527-2	125 Mpa
			ISO 527-1	125 Mpa

Electrical performance	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
Compared to the anti leakage trace index		IEC 60112	PLC 4
Dielectric constant	1KHz	IEC 60250	7.6
Dielectric constant		1MHz	IEC 60250	6.4
Dielectric loss	3mmt	IEC 60243-1	9 KV/mm
Dielectric strength	1MHz	IEC 60250	0.096
		1KHz	IEC 60250	0.021
		3.00mm	IEC 60243-1	9.0 KV/mm
Dissipation factor	1MHz	IEC 60250	0.10
		耐电弧性	IEC 60250	116 sec
		1kHz	IEC 60250	0.020
Leakage Tracking Index (CTI)		IEC 60112	150 V
Relative permittivity	1kHz	IEC 60250	7.60
Relative permittivity		1MHz	IEC 60250	6.40
Surface resistivity		IEC 60093	1×10 Ω
Surface resistivity			ASTM D257/IEC 60093	7.6 Ω
Volume resistivity		IEC 60093	9×10 Ω·cm
			ASTM D257/IEC 60093	9 x 1015 Ω.cm
			IEC 60093	9E+15 ohms·cm

other	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
characteristic			耐薬品性、耐熱水性、耐湿熱性

Physical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
density		ASTM D792/ISO 1183	1.62
Melt viscosity	310°C,1000sec^-1	ISO 11443	200000 mPa·s
Shrinkage rate	Flow，80℃×2mmt		0.4 %
Shrinkage rate		Across Flow，80℃×2mmt		1.0 %
Water absorption rate	23°C,24hr	ISO 62	0.040 %
Water absorption rate			ASTM D570/ISO 62	0.04 %

flammability	Test Condition	Test Method	JAPAN POLYPLASTIC/3130A1
UL flame retardant rating		UL 94	V-0