PC ET3117 021613 COVESTRO GERMANY

Makrolon®

Automotive Applications,Lighting installation,electrical equipment

Flame retardant,High mobility

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Ball Pressure Test		ISO 2039-1	112 Mpa

film	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Carbon dioxide transmittance	23°C, 25.4 μm	ISO 2556	16900 cm³/m²/bar/24 hr
gas transmission rate	Carbon Dioxide : 100.0 μm	ISO 2556	3800 cm³/m²/bar/24 hr
		Nitrogen : 100.0 μm	ISO 2556	120 cm³/m²/bar/24 hr
		Oxygen : 100.0 μm	ISO 2556	650 cm³/m²/bar/24 hr
		Oxygen : 25.4 μm	ISO 2556	2760 cm³/m²/bar/24 hr
		Nitrogen : 25.4 μm	ISO 2556	510 cm³/m²/bar/24 hr
Water vapor permeability	23°C, 85% RH, 100 μm	ISO 15106-1	15 g/m²/24 hr

thermal performance	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Ball Pressure Test	139°C	IEC 60695-10-2	通过
Glass transition temperature		ISO 11357-2	146 °C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	140 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	127 °C
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	6.5E-5 cm/cm/°C
Linear coefficient of thermal expansion		Across Flow : 23 to 55°C	ISO 11359-2	6.5E-5 cm/cm/°C
RTI	1.5 mm	UL 746	125 °C
RTI Elec	1.5 mm	UL 746	125 °C
RTI Imp	1.5 mm	UL 746	115 °C
thermal conductivity	23°C	ISO 8302	0.20 W/m/K
Vicat softening temperature	--	ISO 306/B120	147 °C
Vicat softening temperature		--	ISO 306/B50	146 °C

mechanical properties	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Bending modulus	23°C	ISO 178	2400 Mpa
bending strength	23°C	ISO 178	98.0 Mpa
		23°C	ISO 178	7.0 %
		3.5% Strain, 23°C	ISO 178	74.0 Mpa
Nominal tensile fracture strain	23°C	ISO 527-2/50	> 50 %
Tensile creep modulus	1000 hr	ISO 899-1	1900 Mpa
Tensile creep modulus		1 hr	ISO 899-1	2200 Mpa
Tensile modulus	23°C	ISO 527-2/1	2400 Mpa
Tensile strain	Yield, 23°C	ISO 527-2/50	6.3 %
Tensile strain		Break, 23°C	ISO 527-2/50	130 %
tensile strength	Break, 23°C	ISO 527-2/50	70.0 Mpa
tensile strength		Yield, 23°C	ISO 527-2/50	65.0 Mpa

Electrical performance	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Compared to the anti leakage trace index	Solution A	IEC 60112	V
Compared to the anti leakage trace index		Solution B	IEC 60112	V
Dielectric strength	23°C, 1.00 mm	IEC 60243-1	34 KV/mm
Dissipation factor	23°C, 100 Hz	IEC 60250	1.0E-3
Dissipation factor		23°C, 1 MHz	IEC 60250	9.5E-3
Relative permittivity	23°C, 100 Hz	IEC 60250	3.10
Relative permittivity		23°C, 1 MHz	IEC 60250	3.00
Surface resistivity		IEC 60093	1.0E+16 ohms
Volume resistivity	23°C	IEC 60093	1.0E+16 ohms·cm

Physical properties	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Apparent density		ISO 60	0.66 g/cm³
density	23°C	ISO 1183	1.20 g/cm³
melt mass-flow rate	300°C/1.2 kg	ISO 1133	6.5 g/10 min
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	6.00 cm3/10min
Shrinkage rate	Flow : 2.00 mm4	ISO 294-4	0.70 %
		横向Flow	ISO 2577	0.60 - 0.80 %
		Flow	ISO 2577	0.60 - 0.80 %
		横向Flow : 280°C, 2.00 mm4	ISO 294-4	0.75 %
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.12 %

impact performance	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Charpy Notched Impact Strength	23°C, Partial Break	ISO 179/1eA	80 kJ/m²
Charpy Notched Impact Strength		-30°C, Complete Break	ISO 179/1eA	14 kJ/m²
Impact strength of cantilever beam gap	23°C, Partial Break	ISO 180/A	70 kJ/m²
Impact strength of cantilever beam gap		-30°C, Complete Break	ISO 180/A	20 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
		23°C	ISO 179/1eU	无断裂
		-60°C	ISO 179/1eU	无断裂
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	70.0 J
Multi axis Instrumented Impact Energy		23°C	ISO 6603-2	60.0 J
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6500 N
Multi axis Instrumented Peak Impact Force		23°C	ISO 6603-2	5600 N

flammability	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Application of Flame from Small Burner		DIN 53438-1	K1. F1
auto-ignition temperature		ASTM D1929	550 °C
Burning rate	> 1.00 mm	ISO 3795	passed
Burning wire flammability index	1.5 mm	IEC 60695-2-12	875 °C
		0.75 mm	IEC 60695-2-12	875 °C
		3.0 mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	28 %
flash temperature		ASTM D1929	480 °C
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	875 °C
		3.0 mm	IEC 60695-2-13	900 °C
		0.75 mm	IEC 60695-2-13	875 °C
UL flame retardant rating	1.50 mm	IEC 60695-11-5	1.0 min
		0.75 mm	UL 94	V-2
		1.5 mm	UL 94	HB
		2.00 mm	IEC 60695-11-5	0.1 min
		3.00 mm	IEC 60695-11-5	0.2 min

optical performance	Test Condition	Test Method	COVESTRO GERMANY/ET3117 021613
Electrolytic corrosion	23°C	IEC 60426	A1
Refractive index		ISO 489	1.586
transmissivity	4000 μm	ISO 13468-2	87.0 %
		1000 μm	ISO 13468-2	89.0 %
		3000 μm	ISO 13468-2	88.0 %
		2000 μm	ISO 13468-2	89.0 %
turbidity	3000 μm	ISO 14782	< 0.80 %