Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CP8320-100 SABIC INNOVATIVE US
CYCOLAC™
Electrical applications,Automotive interior parts,Application in the automotive field
High mobility,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| 23°C | ISO 180/1A | 6060 kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6060 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 55.0 J |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂无断裂 |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 3030 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂无断裂 |
| 23°C | ASTM D256 | 600 J/m | |
| -30°C | ASTM D256 | 400 J/m | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂无断裂 |
| -30°C | ISO 180/1A | 3030 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| yield | ASTM D638 | 45.0 Mpa | |
| ASTM D638 | 4.0 % | ||
| ISO 527-2/50 | 45.0 Mpa | ||
| Yield, 50.0mm span | ASTM D790 | 70.0 Mpa | |
| fracture | ISO 527-2/50 | 40.0 Mpa | |
| ASTM D638 | 40.0 Mpa | ||
| ISO 527-2/50 | 100 % | ||
| ASTM D638 | 100 % | ||
| yield | ISO 527-2/50 | 4.0 % | |
| --8 | ISO 178 | 65.0 Mpa | |
| 50.0mm span | ASTM D790 | 2000 Mpa | |
| --1 | ASTM D638 | 2100 Mpa | |
| --7 | ISO 178 | 2000 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 35 KV/mm |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 14 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.30 % | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 13.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/CP8320-100 |
|---|---|---|---|
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 9E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 92.0 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 90.0 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 9E-05 cm/cm/°C |