PBT WFL36-BK1A900 SABIC INNOVATIVE US
LNP™ LUBRICOMP™ 
Plastic bag、Automotive Applications、Industrial applications
High temperature resistan、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/WFL36-BK1A900
Linear thermal expansion coefficientTD：-40到40°CISO11359-26.7E-05 cm/cm/°C
TD：-40到40°CASTME8316.7E-05 cm/cm/°C
MD：-40到40°CISO11359-23.9E-05 cm/cm/°C
Heat Deflection Temperature1.8MPa,未退火,3.20mmASTMD648218 °C
1.8MPa,未退火,64.0mm跨距ISO75-2/Af214 °C
Linear thermal expansion coefficientMD：-40到40°CASTME8313.9E-05 cm/cm/°C
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/WFL36-BK1A900
Moisture Absorption平衡,23°C,50%RHISO620.040 %
24hr,50%RHASTMD5700.040 %
Modeling ShrinkageMD：24小时ASTMD9550.10to0.30 %
TD：24hrASTMD9550.50to1.0 %
TD:24小时ISO294-40.50to1.0 %
MD:24小时ISO294-40.10to0.30 %
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/WFL36-BK1A900
Tensile Elongation断裂ASTMD6382.3 %
Flexural ModulusASTMD79010200 Mpa
Flexural StrengthASTMD790193 Mpa
Tensile ModulusISO527-2/110600 Mpa
Coefficient of FrictionDynamicASTMD3702Modified0.57
Flexural ModulusISO17810000 Mpa
Coefficient of FrictionStaticASTMD3702Modified0.41
Specific Wear RateASTMD3702Modified42.0 10^-10in^5-min/ft-lb-hr
Tensile Strain断裂ISO527-22.2 %
Tensile Stress断裂ISO527-2118 Mpa
Flexural StressISO178187 Mpa
Tensile ModulusASTMD63810300 Mpa
Tensile Strength断裂ASTMD638118 Mpa
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/WFL36-BK1A900
Instrumented Dart Impact23°C,EnergyatPeakLoadASTMD376313.7 J
23°CISO180/1U43 kJ/m²
Notched Izod Impact Strength23°CISO180/1A9.2 kJ/m²
Multi-Axial Instrumented Impact EnergyISO6603-22.61 J