Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS 63000CTC SABIC INNOVATIVE US
LNP™ STAT-KON™
Automotive interior parts、Electrical applications、chip
High mobility、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/63000CTC |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 1170 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 34.0 Mpa |
| elongation | 断裂4 | 内部方法 | 200 % |
| tensile strength | 屈服3 | ASTM D638 | 35.0 Mpa |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 1170 Mpa |
| --6 | ISO 178 | 1150 Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 1190 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 140 % |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 52.0 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/63000CTC |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 8.0E+9-3.0E+11 ohms·cm | |
| Surface Resistivity | ASTM D257 | 9.0E+9-4.0E+11 ohms | |
| StaticDecay | FTMS101B | 2.0 sec |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE US/63000CTC |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | 25 % |
| transmissivity | 2540µm | ASTM D1003 | 77.0 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/63000CTC |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.60 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.70 % |
| Shrinkage rate | TD | 内部方法 | 0.60 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/63000CTC |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 75.0 °C |
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 1.4E-04 cm/cm/°C |
| MD:23到60°C | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 84.0 °C |