PC HFD1034-NA9E109T SABIC INNOVATIVE NANSHA
LEXAN™
Electrical applications、Automotive Applications、Mechanical accessories
Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1034-NA9E109T |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 82 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 78.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 69 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 134 J | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 63 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 72 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1034-NA9E109T |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1034-NA9E109T |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2080 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| tensile strength | 断裂 | ASTM D638 | 67.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| tensile strength | 断裂 | ISO 527-2/50 | 73.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2240 Mpa |
| Tensile modulus | ASTM D638 | 2260 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 98.0 Mpa |
| elongation | 断裂 | ASTM D638 | 140 % |
| bending strength | ISO 178 | 89.0 Mpa | |
| Flexural modulus | ISO 178 | 2070 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 58.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 140 % |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1034-NA9E109T |
|---|---|---|---|
| Haze ratio | 2540µm | ASTM D1003 | <1.0 % |
| refractive index | ASTM D542 | 1.582 | |
| transmissivity | 2540µm | ASTM D1003 | 88.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1034-NA9E109T |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1034-NA9E109T |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 6.50 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.30 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1034-NA9E109T |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 131 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 125 °C |
| vicat | -- | ISO 306/B50 | 130 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 115 °C |
| vicat | ASTM D152510 | 136 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 115 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |