PA66 LAMIGAMID® 200 SCHWARTZ GERMANY
--
Bearings, liners, gears, bushings
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 200 |
|---|---|---|---|
| Impact strength of cantilever beam gap | kJ/m² | >3.0 >15 | |
| Suspended wall beam without notch impact strength | 无断裂 |
| hardness | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 200 |
|---|---|---|---|
| ball-indentation hardness | MPa | 170 100 |
| Mechanical properties | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 200 |
|---|---|---|---|
| tensile strength | 屈服 | MPa | 90.0 60.0 |
| 断裂 | MPa | 135 60.0 | |
| coefficient of friction | 与钢-动态 | 0.020 0.080 | |
| 与钢-静态 | 0.35 0.42 | ||
| Tensile modulus | MPa | 3300 2000 | |
| Tensile strain | 断裂 | % | >40 >150 |
| Flexural modulus | MPa | 2900 2000 |
| Electrical performance | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 200 |
|---|---|---|---|
| dielectric constant | 3.60 5.00 | ||
| Dissipation Factor | 0.026 0.20 | ||
| Surface Resistivity | ohms | 1E+12 1E+10 | |
| dielectric strength | kV/mm | 50 40 |
| physical property | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 200 |
|---|---|---|---|
| density | g/cm³ | 1.15 -- | |
| Water absorption rate | 饱和,23°C | % | 7.5to9.0 -- |
| 23°C,24hr | % | 2.5to3.0 -- |
| Thermal performance | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 200 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 200 -- |
| melting temperature | °C | 255 -- | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 105 -- |
| specific heat | J/kg/°C | 1670 -- | |
| thermal conductivity | W/m/K | 0.20 -- | |
| Linear coefficient of thermal expansion | MD：20到100°C | cm/cm/°C | 7.0E-5到1.0E-4 -- |