Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 4130-104K TAIWAN CHANGCHUN
LONGLITE®
Automotive sector、Electrical field、Electronic field、Home appliance components
Glass fiber reinforced、Flame retardant、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TAIWAN CHANGCHUN/4130-104K |
|---|---|---|---|
| elongation at break | ISO 527 | 125 Mpa | |
| bending strength | ISO 178 | 180 Mpa | |
| Flexural modulus | ISO 178 | 8000 Mpa | |
| elongation at break | ISO 527 | 2.5 % | |
| Simply supported beam without notch impact at 23 ℃ | ISO 179 | 50 | |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 8.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | TAIWAN CHANGCHUN/4130-104K |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 10000000000000 Ω.cm | |
| Surface Resistivity | IEC 60093 | 10000000000000 Ω | |
| dielectric strength | 2.0mm | IEC 60243 | 20 KC/mm |
| Flame retardant performance | Test Condition | Test Method | TAIWAN CHANGCHUN/4130-104K |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 5VA |
| 0.74mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 5VA |
| physical property | Test Condition | Test Method | TAIWAN CHANGCHUN/4130-104K |
|---|---|---|---|
| Shrinkage rate | 流动 | ISO 294 | 0.8-1.2 % |
| ISO 294 | 0.2-0.5 % | ||
| Network Fusion Index 260 ℃ 2.16kg | ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | TAIWAN CHANGCHUN/4130-104K |
|---|---|---|---|
| melting temperature | ISO 11357 | 225 °C | |
| Heat distortion temperature | 未退火0.45MPa，HDT | ISO 75 | 215 °C |
| 未退火1.8MPa，HDT | ISO 75 | 200 °C |