PC/ABS NH-1015V K23608 LOTTE KOREA
INFINO®
Laptop
enhance,transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE KOREA/NH-1015V K23608 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 17 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 14 kJ/m² |
| hardness | Test Condition | Test Method | LOTTE KOREA/NH-1015V K23608 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 118 |
| R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/NH-1015V K23608 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 61.0 Mpa |
| Tensile modulus | ISO 527-2/50 | 2500 Mpa | |
| bending strength | ISO 178 | 89.0 Mpa | |
| Flexural modulus | ISO 178 | 2550 Mpa | |
| bending strength | ASTM D790 | 87.0 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 64.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 45 % |
| Flexural modulus | ASTM D790 | 2400 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 48.0 Mpa |
| flammability | Test Condition | Test Method | LOTTE KOREA/NH-1015V K23608 |
|---|---|---|---|
| UL flame retardant rating | 2.0mm | UL 94 | 5VB |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LOTTE KOREA/NH-1015V K23608 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.50-0.70 % |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 30 g/10min |
| 220°C/10.0kg | ISO 1133 | 30 g/10min |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/NH-1015V K23608 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 82.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 86.0 °C | |
| vicat | -- | ISO 306/B120 | 103 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 94.0 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 97.0 °C | |
| RTI Imp | 1.5mm | UL 746 | 85.0 °C |
| vicat | -- | ISO 306/B50 | 100 °C |
| RTI Str | 1.5mm | UL 746 | 90.0 °C |
| RTI Elec | 1.5mm | UL 746 | 90.0 °C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 102 °C |