PA66 NILAMID® A3 GF30 TM2 Celanese Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 GF30 TM2 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.5 kJ/m² |
| -30°C | ISO 179/1eA | 5.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| -30°C | ISO 179/1eU | 28 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 8.0 kJ/m² |
| -30°C | ISO 180/A | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 GF30 TM2 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.20mm,解决方案A | IEC 60112 | PLC 1 |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | 2.00mm | IEC 60243-1 | 21 kV/mm |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| Mechanical properties | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 GF30 TM2 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 135 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 8500 MPa |
| flammability | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 GF30 TM2 |
|---|---|---|---|
| Burning wire flammability index | 0.8mm | IEC 60695-2-12 | 650 °C |
| 3.2mm | IEC 60695-2-12 | 650 °C | |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 0.8mm | UL 94 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 GF30 TM2 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.37 g/cm³ |
| Shrinkage rate | TD:23°C | ISO 294-4 | 0.80 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 % |
| Shrinkage rate | MD:23°C | ISO 294-4 | 0.30 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 5.0 % |
| Thermal performance | Test Condition | Test Method | Celanese Corporation/NILAMID® A3 GF30 TM2 |
|---|---|---|---|
| Continuous use temperature | IEC 60216 | 110 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 260 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 254 °C | |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | 通过 |
| 125°C | IEC 60695-10-2 | 通过 |