PPS 0220U9-HD9100 JAPAN POLYPLASTIC
DURAFIDE®
Fitness equipment、sporting goods
High impact resistance、Glass fiber reinforced、 High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/0220U9-HD9100 |
|---|---|---|---|
| ColorNumber | HD9100 |
| Basic performance | Test Condition | Test Method | JAPAN POLYPLASTIC/0220U9-HD9100 |
|---|---|---|---|
| Water absorption rate | 23℃,水中24小时 | ISO 62 | 0.01 % |
| melt viscosity | 310℃,1000/sec | ISO 11443 | 500 Pa·s |
| density | ISO 1183 | 1.31 g/cm |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/0220U9-HD9100 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 21 % | |
| bending strength | ISO 178 | 120 Mpa | |
| Flexural modulus | ISO 178 | 3400 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 7.0 KJ/m | |
| fracture strain | ISO 527-1 | 21 % | |
| tensile strength | ISO 527-1 | 75 Mpa | |
| ISO 527-2 | 75.0 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/0220U9-HD9100 |
|---|---|---|---|
| relative permittivity | 1kHz | IEC 60250 | 3.50 |
| dielectric strength | 1MHz | IEC 60250 | 0.002 |
| 1KHz | IEC 60250 | 0.001 | |
| dielectric constant | 1MHz | IEC 60250 | 3.5 |
| dielectric strength | 3.00mm | IEC 60243-1 | 18 KV/mm |
| dielectric constant | 1KHz | IEC 60250 | 3.5 |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Volume resistivity | IEC 60093 | 2×10 Ω·cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 2E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Dielectric loss | 3mmt | IEC 60243-1 | 18 KV/mm |
| Dissipation Factor | 1kHz | IEC 60250 | 1E-03 |
| 耐电弧性 | IEC 60250 | 111 sec | |
| Volume resistivity | IEC 60093 | 2E+16 ohms·cm | |
| Surface Resistivity | IEC 60093 | 8×10 Ω | |
| Leakage Tracking Index (CTI) | IEC 60112 | 125 V |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/0220U9-HD9100 |
|---|---|---|---|
| Shrinkage rate | 流动方向，80℃×2mmt | 1.1 % | |
| 垂直方向，80℃×2mmt | 1.6 % | ||
| Water absorption rate | 23°C,24hr | ISO 62 | 0.040 % |
| melt viscosity | 310°C,1000sec^-1 | ISO 11443 | 500000 mPa·s |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/0220U9-HD9100 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD | 内部方法 | 6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-1 | 95 °C |
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359-2 | 4 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 95.0 °C |
| Linear coefficient of thermal expansion | MD | 内部方法 | 5E-05 cm/cm/°C |
| 垂直方向 | - | 6 |