Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

LCP A430 VF3001 CELANESE USA
VECTRA®
Automotive Applications、Home appliance components
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | CELANESE USA/A430 VF3001 |
---|---|---|---|
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 67 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 86 kJ/m² |
hardness | Test Condition | Test Method | CELANESE USA/A430 VF3001 |
---|---|---|---|
Rockwell hardness | M级 | ISO 2039-2 | 55 |
Electrical performance | Test Condition | Test Method | CELANESE USA/A430 VF3001 |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
dielectric strength | IEC 60243-1 | 36 KV/mm | |
Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
Dissipation Factor | 100Hz | IEC 60250 | 0.030 |
arc resistance | 内部方法 | 130 sec | |
relative permittivity | 100Hz | IEC 60250 | 3.30 |
1MHz | IEC 60250 | 2.70 | |
Surface Resistivity | IEC 60093 | 1E+15 ohms | |
Dissipation Factor | 1MHz | IEC 60250 | 0.016 |
Mechanical properties | Test Condition | Test Method | CELANESE USA/A430 VF3001 |
---|---|---|---|
Tensile modulus | ISO 527-2/1A/1 | 7000 Mpa | |
bending strength | 23°C | ISO 178 | 125 Mpa |
Compression Modulus | ISO 604 | 6000 Mpa | |
Flexural modulus | 23°C | ISO 178 | 7100 Mpa |
Compressive Stress | 1%Strain | ISO 604 | 38.0 Mpa |
tensile strength | 断裂 | ISO 527-2/1A/5 | 156 Mpa |
Tensile strain | 断裂 | ISO 527-2/1A/5 | 6.2 % |
flammability | Test Condition | Test Method | CELANESE USA/A430 VF3001 |
---|---|---|---|
UL flame retardant rating | UL 94 | V-0 |
physical property | Test Condition | Test Method | CELANESE USA/A430 VF3001 |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 0.70 % |
MD | ISO 294-4 | 0.0 % |
Thermal performance | Test Condition | Test Method | CELANESE USA/A430 VF3001 |
---|---|---|---|
melting temperature | ISO 11357-3 | 280 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 227 °C |
vicat | ISO 306/B50 | 138 °C | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 165 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-06 cm/cm/°C |
Heat distortion temperature | 8.0MPa,未退火,HDT | ISO 75-2/C | 89.0 °C |
Linear coefficient of thermal expansion | TD | ISO 11359-2 | 4.6E-05 cm/cm/°C |