Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL9112 GY1C184 SABIC INNOVATIVE JAPAN
LEXAN™ 
Electronic and Electrical、Plastic bag、lens、Industrial applications
High mobility、Ductility at low temperat、Short molding cycle
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE JAPAN/EXL9112 GY1C184
Dart impact equipped with measuring instruments23°C, Total EnergyASTM D376367.0 J
Impact strength of simply supported beam gap 7-30°CISO 179/1eA25 kJ/m²
Unscented Izod Impact Strength 8-30°CISO 180/1U无断裂
Impact strength of simply supported beam gap 723°CISO 179/1eA60 kJ/m²
Unscented Izod Impact Strength 823°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE JAPAN/EXL9112 GY1C184
H 358/30ISO 2039-195.0 Mpa
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE JAPAN/EXL9112 GY1C184
tensile strength屈服ISO 527-2/5059.0 Mpa
Bending stress-- 5, 6ISO 17888.0 Mpa
elongation断裂ISO 527-2/50100 %
Flexural modulus-- 5ISO 1782300 Mpa
elongation屈服 3ASTM D6385.8 %
Bending stress屈服, 50.0 mm 跨距 4ASTM D79095.0 Mpa
Tensile modulus-- 2ASTM D6382260 Mpa
tensile strength屈服 3ASTM D63858.0 Mpa
断裂ISO 527-2/5055.0 Mpa
elongation屈服ISO 527-2/505.0 %
Flexural modulus50.0 mm 跨距 4ASTM D7902330 Mpa
Tensile modulus--ISO 527-2/12200 Mpa
elongation断裂 3ASTM D638100 %
tensile strength断裂 3ASTM D63858.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE JAPAN/EXL9112 GY1C184
CTIIEC 60112175 V
Dissipation Factor1 MHzIEC 602500.010
1 MHzIEC 602502.70
Dissipation Factor60 HzIEC 602504.0E-4
50 HzIEC 602504.0E-4
50 HzIEC 602502.70
dielectric strength3.20 mm, 在油中IEC 60243-119 KV/mm
60 HzIEC 602502.70
flammabilityTest ConditionTest MethodSABIC INNOVATIVE JAPAN/EXL9112 GY1C184
UL flame retardant rating3.0 mmUL 945VA
Hot filament ignition temperature1.0 mmIEC 60695-2-13825 °C
UL flame retardant rating1.5 mmUL 94V-0
Burning wire flammability index1.0 mmIEC 60695-2-12960 °C
Limiting Oxygen IndexISO 4589-240 %
physical property Test ConditionTest MethodSABIC INNOVATIVE JAPAN/EXL9112 GY1C184
Water absorption rate平衡, 23°C, 50% RHISO 620.15 %
Shrinkage rate横向流动 : 3.20 mm内部方法0.40 到 0.80 %
Outdoor applicabilityUL 746Cf1
Molten Volume Flow Rate (MVR)300°C/1.2 kgISO 113316.0 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123817 g/10 min
Shrinkage rate流动 : 3.20 mm内部方法0.40 到 0.80 %
Water absorption rate饱和, 23°CISO 620.35 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE JAPAN/EXL9112 GY1C184
Thermal deformation temperature under load0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10ISO 75-2/Be136 °C
流动 : 23 到 80°CISO 11359-27.5E-5 cm/cm/°C
流动 : -40 到 40°CASTM E8317.2E-5 cm/cm/°C
Thermal deformation temperature under load0.45 MPa, 未退火, 3.20 mmASTM D648136 °C
RTIUL 746130 °C
Thermal deformation temperature under load1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10ISO 75-2/Ae124 °C
vicat--ASTM D152511, ISO 306/B5011143 °C
--ISO 306/B120144 °C
横向 : 23 到 80°CISO 11359-27.5E-5 cm/cm/°C
横向 : -40 到 40°CASTM E8317.2E-5 cm/cm/°C
Thermal deformation temperature under load1.8 MPa, 未退火, 3.20 mmASTM D648123 °C
Ball Pressure Test123 到 127°CIEC 60695-10-2通过
RTI ImpUL 746120 °C
RTI ElecUL 746130 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE JAPAN/EXL9112 GY1C184
Processing (melt) temperature295 到 315 °C
drying temperature120 °C
Exhaust hole depth0.025 到 0.076 mm
Temperature at the front of the material cylinder295 到 315 °C
Suggested maximum moisture content0.020 %
Temperature in the middle of the barrel280 到 305 °C
Temperature70 到 95 °C
screw speed40 到 70 rpm
Temperature at the rear of the barrel215 到 295 °C
Back pressure0.300 到 0.700 Mpa
drying time3.0 到 4.0 hr
Suggested injection volume40 到 60 %
Spray nozzle temperature290 到 310 °C