PA66 14G43 ASAHI JAPAN
Leona™
Electrical field、Electronic field
Glass fiber reinforced、High rigidity、high strength、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/14G43 |
|---|---|---|---|
| Water absorption rate | 湿 | 1.4 % | |
| Shrinkage rate | 乾，3mm厚，平行/垂直于流动方向 | 0.3-0.7 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/14G43 |
|---|---|---|---|
| Flexural modulus | 乾（湿） | ASTM D-790 | 120.000（85.000） Kgf/cm |
| Taber wear resistance | 湿 | ASTM D-1044 | 1900 mg/1000次 |
| bending strength | 乾（湿） | ASTM D-790 | 3200（2400） Kgf/cm |
| (fracture) elongation rate | 乾（湿） | ASTM D-638 | 3（4） % |
| tensile strength | 乾（湿） | ASTM D-638 | 2000（1600） Kgf/cm |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 127 kg·cm/cm(J/M)ft·lb/in | |
| Flexural modulus | ASTM D790/ISO 178 | 11770 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 214 kg·cm/cm(J/M)ft·lb/in | |
| Impact strength of cantilever beam gap | 乾（湿） | ASTM D-256 | 13（21） Kgf.cm/cm |
| Rockwell hardness | ASTM D785 | M96 | |
| 乾（湿） | ASTM D-785 | 96/118（80） M/R |
| other | Test Condition | Test Method | ASAHI JAPAN/14G43 |
|---|---|---|---|
| characteristic | 高钢性耐热 | ||
| purpose | 自动车部件 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/14G43 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.50 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.4 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/14G43 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 乾 | ASTM D696 | 3 1e-5/cm.°C |
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 250 ℃（℉） |
| 乾，HDT | ASTM D648 | 250（260） °C 18.2kgf/cm | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 3 mm/mm.℃ | |
| UL flame retardant rating | UL 94 | HB |