Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A RV200K RADICI SUZHOU
Radilon® 
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodRADICI SUZHOU/A RV200K
Impact strength of simply supported beam without notch23°CISO 179/1eU45 kJ/m²
-30°CISO 179/1eU40 kJ/m²
Mechanical propertiesTest ConditionTest MethodRADICI SUZHOU/A RV200K
Tensile modulusISO 527-2/1A/16900 Mpa
bending strengthISO 178210 Mpa
Flexural modulusISO 1786300 Mpa
tensile strength 断裂ISO 527-2/1A/5140 Mpa
Tensile strain断裂ISO 527-2/1A/53.0 %
Electrical performanceTest ConditionTest MethodRADICI SUZHOU/A RV200K
Volume resistivityIEC 600931.0E+15 ohms·cm
Compared to the Leakage Tracking Index (CTI)解决方案 AIEC 60112PLC 1
Surface ResistivityIEC 600931.0E+12 ohms
flammabilityTest ConditionTest MethodRADICI SUZHOU/A RV200K
Burning wire flammability index2.0 mmIEC 60695-2-12700 °C
flammabilityFMVSS 3020 mm/min
UL flame retardant rating0.8 mmUL 94HB
physical property Test ConditionTest MethodRADICI SUZHOU/A RV200K
Water absorption rate饱和, 23°C, 2.00 mmISO 627.8 %
平衡, 23°C, 2.00 mm, 50% RHISO 622.1 %
Shrinkage rate流量ISO 294-40.40 %
横向流量ISO 294-40.90 %
Thermal performanceTest ConditionTest MethodRADICI SUZHOU/A RV200K
melting temperatureISO 11357-3260 °C
Heat distortion temperature1.8 MPa, 未退火，HDTISO 75-2/Af220 °C
vicatISO 306/B50240 °C
injectionTest ConditionTest MethodRADICI SUZHOU/A RV200K
Suggested maximum moisture content0.15 %
Drying time - hot air dryer2.0 to 4.0 hr
Processing (melt) temperature280 to 300 °C
Dew Point - Hot Air Drying Machine-20 °C
Temperature80 to 100 °C
injection speed中等偏快
Drying temperature - hot air dryer80 °C