PC HL-7001 MITSUBISHI THAILAND
IUPILON™ 
Medical Supplies,Home appliance components
High mobility
TDS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI THAILAND/HL-7001
Charpy Notched Impact Strength23°CISO 17912 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179无断裂
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/HL-7001
dielectric strength1.00mmIEC 60243-131 KV/mm
Volume resistivityIEC 600933E+16 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602506E-04
dielectric strength3.00mmIEC 60243-118 KV/mm
relative permittivity1MHzIEC 602503.10
Surface ResistivityIEC 600936E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
Dissipation Factor1MHzIEC 602509E-03
Mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/HL-7001
Tensile modulusISO 527-22300 Mpa
Nominal tensile fracture strainISO 527-287 %
bending strengthISO 178100 Mpa
Flexural modulusISO 1782500 Mpa
Tensile strain屈服ISO 527-25.5 %
tensile strength 屈服ISO 527-264.0 Mpa
flammabilityTest ConditionTest MethodMITSUBISHI THAILAND/HL-7001
UL flame retardant rating0.38mmUL 94V-2
physical property Test ConditionTest MethodMITSUBISHI THAILAND/HL-7001
Shrinkage rateTD:3.20mm0.40-0.60 %
Melt volume flow rate300°C/1.2kgISO 1133108 cm3/10min
Shrinkage rate吸水率(饱和,23°C)0.24 %
MD:3.20mm0.40-0.60 %
densityISO 11831.20 g/cm³
melt mass-flow rate300°C/1.2kgISO 1133110 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/HL-7001
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B132 °C
1.8MPa,未退火，HDTISO 75-2/A118 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
TDISO 11359-26.6E-05 cm/cm/°C