Certificates
PC DFL-4022 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Casters、Electronic and Electrical
Easy to demould、Easy to form
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4022 |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 140 °C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 146 °C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831,ISO11359-2 | 5.6E-05 cm/cm/°C |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 140 °C | |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831,ISO11359-2 | 5.6E-05 cm/cm/°C |
| 0.45MPa, Unannealed,3.20mm | ASTMD648 | 145 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4022 |
|---|---|---|---|
| ASTMD638 | 4140 Mpa | ||
| fracture | 67.6 Mpa | ||
| ISO527-2 | 67.0 Mpa | ||
| 5.8 % | |||
| Coefficient of Friction | 与自身-静态 | ASTMD3702Modified | 0.44 |
| Specific Wear Rate | 166 10^-10in^5-min/ft-lb-hr | ||
| yield | ASTMD638,ISO527-2 | 3.3 % | |
| fracture | ASTMD638 | 5.5 % | |
| yield | 71.7 Mpa | ||
| ISO527-2 | 71.0 Mpa | ||
| Flexural Stress | ISO178 | 118 Mpa | |
| Coefficient of Friction | 与自身-动态 | ASTMD3702Modified | 0.38 |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4022 |
|---|---|---|---|
| Flow:24hr | ISO294-4 | 0.50 % | |
| ASTMD955 | 0.60到0.80 % | ||
| Across Flow:24hr | ISO294-4 | 0.65 % | |
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.10 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL-4022 |
|---|---|---|---|
| ASTMD3763 | 23.2 J | ||
| ASTMD256 | 140 J/m | ||
| ASTMD4812 | 740 J/m | ||
| ISO180/1A | 13 kJ/m² | ||
| ISO180/1U | 49 kJ/m² |