PEI
PEI SABIC INNOVATIVE NANSHA HU1010 7H1D395
Injection grade
US$ 12,300 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HU1010 7H1D395
elongationBreakASTM D63860 %
bending strengthISO 178160 Mpa
Yield,50.0mmSpan5ASTM D790174 Mpa
Tensile strainBreakISO 527-2/560 %
Tensile modulusASTM D6383580 Mpa
tensile strengthBreakASTM D638105 Mpa
YieldISO 527-2/5105 Mpa
Bending modulus50.0mmSpan5ASTM D7903420 Mpa
ISO 1783300 Mpa
elongationYieldASTM D6387.0 %
Tensile strainYieldISO 527-2/56.0 %
bending strengthYield,100mmSpan4ASTM D790165 Mpa
Tensile modulusISO 527-2/13200 Mpa
tensile strengthYieldASTM D638110 Mpa
Bending modulus100mmSpan4ASTM D7903520 Mpa
Taber abraser1000Cycles,1000g,CS-17WheelASTM D104410.0 mg
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HU1010 7H1D395
Dart impact23°CASTM D302933.9 J
Impact strength of cantilever beam gap3.20mmASTM D2561200 J/m
23°CISO 180/1A5.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA3.0 kJ/m²
Dart impact23°C,TotalEnergyASTM D376333.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A5.0 kJ/m²
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HU1010 7H1D395
thermal conductivityASTMC1770.22 W/m/K
Linear coefficient of thermal expansionTD：-40to40°CASTME8315E-05 cm/cm/°C
RTI StrUL 746170 °C
Linear coefficient of thermal expansionMD：-20to150°CASTME8315.6E-05 cm/cm/°C
TD：-40to40°CISO 11359-25E-05 cm/cm/°C
Vicat softening temperature--ISO 306/B50211 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af193 °C
1.8MPa,Unannealed,6.40mmASTM D648199 °C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-25E-05 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648207 °C
Vicat softening temperatureASTM D152511219 °C
RTI ElecUL 746170 °C
RTI ImpUL 746170 °C
Vicat softening temperature--ISO 306/B120212 °C
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HU1010 7H1D395
Dielectric strength1.60mm,in OilASTM D14928 KV/mm
Hot wire ignitionHWIUL 746PLC 1
Dielectric constant1kHzASTM D1503.15
Compared to the anti leakage trace indexCTIUL 746PLC 4
High arc combustion indexHAIUL 746PLC 3
Dissipation factor2.45GHzASTM D1502.5E-03
High voltage arc tracing rateHVTRUL 746PLC 2
Volume resistivityASTM D2571E+17 ohms·cm
Arc resistanceASTM D495PLC 5
Dissipation factor1kHzASTM D1501.3E-03
Dielectric strength1.60mm,inAirASTM D14933 KV/mm
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HU1010 7H1D395
Extreme Oxygen IndexASTM D286344 %
UL flame retardant rating0.71mmUL 94V-2
0.75mmUL 94V-0
NBSSmokeDensity-Flaming,Ds,4minASTME6622.00
UL flame retardant rating3.0mmUL 945VA
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HU1010 7H1D395
Melt Volume Flow Rate (MVR)360°C/5.0kgISO 113325.0 cm3/10min
Water absorption rateEquilibrium,23°CASTM D5701.3 %
melt mass-flow rate337°C/6.6kgASTM D123818 g/10min
Water absorption rateEquilibrium,23°C,50%RHISO 620.70 %
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 621.3 %
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/HU1010 7H1D395
Rockwell hardnessM-ScaleASTM D785109

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China