PEI HU1010 7H1D395 SABIC INNOVATIVE NANSHA

ULTEM™

Medical devices,Medical and nursing supplies

Middle flow,Biocompatibility,Steam sterilization

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Rockwell hardness	M-Scale	ASTM D785	109

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	199 °C
		1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	193 °C
		0.45MPa,Unannealed,6.40mm	ASTM D648	207 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	5E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	5E-05 cm/cm/°C
		MD：-20to150°C	ASTME831	5.6E-05 cm/cm/°C
		MD：-40to40°C	ISO 11359-2	5E-05 cm/cm/°C
RTI Elec		UL 746	170 °C
RTI Imp		UL 746	170 °C
RTI Str		UL 746	170 °C
thermal conductivity		ASTMC177	0.22 W/m/K
Vicat softening temperature	--	ISO 306/B120	212 °C
		--	ISO 306/B50	211 °C
			ASTM D152511	219 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Bending modulus	50.0mmSpan5	ASTM D790	3420 Mpa
			ISO 178	3300 Mpa
		100mmSpan4	ASTM D790	3520 Mpa
bending strength	Yield,50.0mmSpan5	ASTM D790	174 Mpa
			ISO 178	160 Mpa
		Yield,100mmSpan4	ASTM D790	165 Mpa
elongation	Break	ASTM D638	60 %
elongation		Yield	ASTM D638	7.0 %
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	10.0 mg
Tensile modulus		ASTM D638	3580 Mpa
Tensile modulus			ISO 527-2/1	3200 Mpa
Tensile strain	Break	ISO 527-2/5	60 %
Tensile strain		Yield	ISO 527-2/5	6.0 %
tensile strength	Yield	ASTM D638	110 Mpa
		Yield	ISO 527-2/5	105 Mpa
		Break	ASTM D638	105 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index	CTI	UL 746	PLC 4
Dielectric constant	1kHz	ASTM D150	3.15
Dielectric strength	1.60mm,inAir	ASTM D149	33 KV/mm
Dielectric strength		1.60mm,in Oil	ASTM D149	28 KV/mm
Dissipation factor	1kHz	ASTM D150	1.3E-03
Dissipation factor		2.45GHz	ASTM D150	2.5E-03
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 2
Hot wire ignition	HWI	UL 746	PLC 1
Volume resistivity		ASTM D257	1E+17 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/HU1010 7H1D395
melt mass-flow rate	337°C/6.6kg	ASTM D1238	18 g/10min
Melt Volume Flow Rate (MVR)	360°C/5.0kg	ISO 1133	25.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.70 %
		Saturation,23°C	ISO 62	1.3 %
		Equilibrium,23°C	ASTM D570	1.3 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.0 kJ/m²
Dart impact	23°C	ASTM D3029	33.9 J
Dart impact		23°C,TotalEnergy	ASTM D3763	33.0 J
Impact strength of cantilever beam gap	3.20mm	ASTM D256	1200 J/m
		-30°C	ISO 180/1A	5.0 kJ/m²
		23°C	ISO 180/1A	5.0 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/HU1010 7H1D395
Extreme Oxygen Index		ASTM D2863	44 %
NBSSmokeDensity-Flaming,Ds,4min		ASTME662	2.00
UL flame retardant rating	0.75mm	UL 94	V-0
		3.0mm	UL 94	5VA
		0.71mm	UL 94	V-2