Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PUR-Ether/PPDI Ultralast™ PE541 CHEMTURU USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE541 |
|---|---|---|---|
| Dynamic Properties | TangentDelta:30°C | 0.0360 | |
| StorageModulus:150°C | 4.98E+08 dynes/cm² | ||
| TangentDelta:150°C | 0.0370 | ||
| StorageModulus:30°C | 8.88E+08 dynes/cm² |
| hardness | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE541 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 53to55 |
| film | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE541 |
|---|---|---|---|
| Tear resistance of pants | ASTM D1938 | 129 N/mm |
| Mechanical properties | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE541 |
|---|---|---|---|
| Wear resistance - DIN | DIN 53516 | 46.0 mm³ | |
| Flexural modulus | ASTM D790 | 183 MPa |
| physical property | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE541 |
|---|---|---|---|
| Shrinkage rate | TD:24小时 | ASTM D955 | 1.3 % |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 15to45 g/10min |
| density | ASTM D792 | 1.13 g/cm³ | |
| Shrinkage rate | MD:24小时 | ASTM D955 | 1.3 % |
| elastomer | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE541 |
|---|---|---|---|
| elongation | 断裂 | ASTM D412 | 840 % |
| tear strength | 开裂 | ASTM D470 | 54 kN/m |
| Shore hardness | ASTM D2632 | 50 % | |
| tensile strength | ASTM D412 | 45.1 MPa | |
| compression set | 70°C,22hr | ASTM D395B | 34 % |
| tensile strength | 100%应变 | ASTM D412 | 15.4 MPa |
| Thermal performance | Test Condition | Test Method | CHEMTURU USA/Ultralast™ PE541 |
|---|---|---|---|
| vicat | ASTM D1525 | 194 °C | |
| Glass Transition Temperature | -45.0 °C |