Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS XR401 9001 LG CHEM KOREA
--
Automotive sector、Electronic field、Automotive interior parts、Automotive External Parts、Shell
heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | LG CHEM KOREA/XR401 9001 |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 112 | |
| R级 | ASTM D785 | 110 |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/XR401 9001 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 49.0 Mpa |
| bending strength | ISO 178 | 75.0 Mpa | |
| elongation | 断裂,3.20mm | ASTM D638 | 20 % |
| Flexural modulus | ISO 178 | 2350 Mpa | |
| tensile strength | 屈服,3.20mm | ASTM D638 | 49.0 Mpa |
| Flexural modulus | 3.20mm | ASTM D790 | 2550 Mpa |
| bending strength | 3.20mm | ASTM D790 | 78.5 Mpa |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/XR401 9001 |
|---|---|---|---|
| Volume resistivity | 23°C | ASTM D257 | 1.5E+03 ohms·cm |
| arc resistance | ASTM D495 | PLC6 | |
| dielectric strength | 23°C,1.00mm | ASTM D149 | 33 KV/mm |
| flammability | Test Condition | Test Method | LG CHEM KOREA/XR401 9001 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | LG CHEM KOREA/XR401 9001 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40-0.70 % |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 9.0 g/10min |
| Shrinkage rate | MD：3.20mm | ISO 294-4 | 0.40-0.70 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 9.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/XR401 9001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 97.0 °C |
| Linear coefficient of thermal expansion | MD：23到60°C | ISO 11359-2 | 8.0E-5to9.0E-5 cm/cm/°C |
| vicat | ASTM D15256 | 106 °C | |
| ISO 306/B50 | 106 °C | ||
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 106 °C |
| 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/Be | 95.0 °C | |
| RTI Imp | UL 746 | 60.0 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/Ae | 88.0 °C |
| Linear coefficient of thermal expansion | TD：23to60°C | ISO 11359-2 | 8.0E-5to9.0E-5 cm/cm/°C |
| RTI Str | UL 746 | 60.0 °C | |
| RTI Elec | UL 746 | 60.0 °C |