PA66 Huafon T23H Huafon Group Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Huafon Group Co., Ltd./Huafon T23H |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 5.9 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Huafon Group Co., Ltd./Huafon T23H |
|---|---|---|---|
| tensile strength | ISO 527-2 | 76.1 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 56 % |
| Flexural modulus | ISO 178 | 2690 MPa | |
| bending strength | ISO 178 | 101 MPa |
| flammability | Test Condition | Test Method | Huafon Group Co., Ltd./Huafon T23H |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-2 |
| 1.0mm | UL 94 | V-2 | |
| 1.6mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Huafon Group Co., Ltd./Huafon T23H |
|---|---|---|---|
| Particle size | 内部方法 | 1.70to2.30 g/100pellets | |
| melt mass-flow rate | 275°C/2.16kg | ISO 1133 | 130 g/10min |
| water content | 内部方法 | <5000 mg/kg | |
| relative viscosity | 内部方法 | 2.30to2.40 |
| Thermal performance | Test Condition | Test Method | Huafon Group Co., Ltd./Huafon T23H |
|---|---|---|---|
| vicat | ISO 306/B120 | 239 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 66.9 °C |
| melting temperature | ASTM D3418 | 263 °C | |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 192 °C |