POM TARNOFORM200 GRUPA AZOTY POLAND
TARNOFORM®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | GRUPA AZOTY POLAND/TARNOFORM200 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180 | 8 kJ/m² | |
| Impact strength of simply supported beam without notch | ---- | ISO 179/1eU | 无断裂 |
| -30°C | ISO 179/1eU | 200 kJ/m² |
| Supplementary Information | Test Condition | Test Method | GRUPA AZOTY POLAND/TARNOFORM200 |
|---|---|---|---|
| ISO TypeISO Type | ISO 1874 | POM-K. M-GNR. 01-02 |
| Electrical performance | Test Condition | Test Method | GRUPA AZOTY POLAND/TARNOFORM200 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1000000000000000 ohms·cm | |
| dielectric constant | 1 Hz1 Hz | IEC 60250 | 3.8 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 0 |
| dielectric strength | 2 mm2.00 mm | IEC 60243-1 | 25 KV/mm |
| Surface Resistivity | IEC 60093 | 100000000000000 ohms |
| Mechanical properties | Test Condition | Test Method | GRUPA AZOTY POLAND/TARNOFORM200 |
|---|---|---|---|
| Tensile modulus | ISO 527-1-2 | 2600 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60 Mpa |
| Tensile strain | 屈服Yield | ISO 527-2/50 | 14 % |
| bending strength | ISO 178 | 60 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 140 Mpa |
| Tensile strain | 断裂Break | ISO 527-2/50 | 50 % |
| Flame retardant performance | Test Condition | Test Method | GRUPA AZOTY POLAND/TARNOFORM200 |
|---|---|---|---|
| burning rate | FMVSS 302 | < 100 mm/min | |
| UL flame retardant rating | 3.20 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | GRUPA AZOTY POLAND/TARNOFORM200 |
|---|---|---|---|
| Melt volume flow rate | 190℃，2.16 kg | ISO 1133 | 2.2 cm3/10min |
| Shrinkage rate | MD：2.0 mm | ISO 294-4 | 2 % |
| Water absorption rate | 平衡，23℃，50% RH | ISO 62 | 0.2 % |
| melt mass-flow rate | 190℃，2.16kg1 | ISO 1133 | 2.5 g/10min |
| density | ISO 1183 | 1.41 g/cm³ | |
| Water absorption rate | 饱和，23℃ | ISO 62 | 0.8 % |
| Thermal performance | Test Condition | Test Method | GRUPA AZOTY POLAND/TARNOFORM200 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 167 °C | |
| vicat | ISO 306/B | 150 °C | |
| Heat distortion temperature | 1.8 MPa，未退火，HDT | ISO 75-2/A | 105 °C |
| Linear coefficient of thermal expansion | MD：23~55℃ | ISO 11359-2 | 0.00011 1/℃ |