hardnessTest ConditionTest MethodSABIC INNOVATIVE US/HPS1R-1124
Ball Pressure TestH358/30ISO 2039-195.0 Mpa
Rockwell hardnessM计秤ASTM D78570
R计秤ASTM D785118
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/HPS1R-1124
Ball Pressure Test125°CIEC 60695-10-2Pass
Hot deformation temperature0.45MPa,未退火,6.40mmASTM D648138 °C
0.45MPa,Unannealed,100mmSpanISO 75-2/Be133 °C
1.8MPa,Unannealed,100mmSpanISO 75-2/Ae121 °C
1.8MPa,未退火,6.40mmASTM D648127 °C
Linear coefficient of thermal expansionMD：-40到95°CASTME8316.8E-05 cm/cm/°C
MD：23到80°CISO 11359-27E-05 cm/cm/°C
specific heatASTMC3511260 J/kg/°C
thermal conductivityASTMC1770.19 W/m/K
ISO 83020.20 W/m/K
Vicat softening temperature--ISO 306/B120140 °C
--ISO 306/B50139 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/HPS1R-1124
Bending modulusISO 1782300 Mpa
50.0mm跨距ASTM D7902310 Mpa
bending strengthISO 17890.0 Mpa
屈服,50.0mm跨距ASTM D79093.1 Mpa
elongation断裂ASTM D638120 %
屈服ASTM D6386.0 %
Taber abraser1000Cycles,1000g,CS-17转轮ASTM D104410.0 mg
Tensile modulusASTM D6382380 Mpa
ISO 527-2/12350 Mpa
Tensile strain断裂ISO 527-2/5070 %
屈服ISO 527-2/506.0 %
tensile strength断裂ISO 527-2/5050.0 Mpa
屈服ASTM D63862.1 Mpa
屈服ISO 527-2/5063.0 Mpa
断裂ASTM D63865.5 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/HPS1R-1124
Dielectric constant1MHzASTM D1502.96
50HzASTM D1503.17
60HzASTM D1503.17
Dielectric strength3.20mm,inAirASTM D14915 KV/mm
3.20mm,在油中IEC 60243-117 KV/mm
Dissipation factor1MHzIEC 602500.010
50HzIEC 602501E-03
1MHzASTM D1500.010
60HzASTM D1509E-04
50HzASTM D1509E-04
60HzIEC 602501E-03
Relative permittivity60HzIEC 602502.70
50HzIEC 602502.70
1MHzIEC 602502.70
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityASTM D257>1.0E+17 ohms·cm
IEC 60093>1.0E+15 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/HPS1R-1124
melt mass-flow rate300°C/1.2kgASTM D123825 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 113323.0 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.50-0.70 %
Specific volumeASTM D7920.835 cm³/g
Water absorption rate平衡,100°CASTM D5700.58 %
24hrASTM D5700.15 %
平衡,23°CASTM D5700.35 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/HPS1R-1124
Charpy Notched Impact Strength23°CISO 179/1eA12 kJ/m²
-30°CISO 179/1eA10 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D376354.2 J
23°CASTM D3029169 J
Impact strength of cantilever beam gap-30°CISO 180/1A10 kJ/m²
23°CISO 180/1A12 kJ/m²
ASTM D1822378 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
23°CISO 180/1UNoBreak
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/HPS1R-1124
Extreme Oxygen IndexISO 4589-225 %
optical performanceTest ConditionTest MethodSABIC INNOVATIVE US/HPS1R-1124
Refractive indexASTM D5421.586
transmissivity2540µmASTM D100388.0 %
turbidity2540µmASTM D10031.0 %