VLDPE CH D0 VERSALIS ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
film | Test Condition | Test Method | VERSALIS ITALY/CH D0 |
---|---|---|---|
Tensile modulus | 1%Secant,MD:CastFilm | ISO 527-3 | 50.0 MPa |
Elmendorf tear strength | MD | ISO 6383-2 | 50.0 kN/m |
film thickness | 8to50µm | ||
elongation | MD:断裂,挤塑薄膜 | ISO 527-3 | 600 % |
tensile strength | MD:断裂,挤塑薄膜 | ISO 527-3 | 43.0 MPa |
MD:Yield,CastFilm | ISO 527-3 | 5.00 MPa | |
Dart impact | 铸造薄膜 | ISO 7765-1/A | 200 g |
Elmendorf tear strength | TD | ISO 6383-2 | 115.0 kN/m |
tensile strength | TD:Yield,CastFilm | ISO 527-3 | 5.00 MPa |
TD:断裂,挤塑薄膜 | ISO 527-3 | 31.0 MPa | |
Tensile modulus | 1%Secant,TD:CastFilm | ISO 527-3 | 60.0 MPa |
elongation | TD:断裂,挤塑薄膜 | ISO 527-3 | 850 % |
Mechanical properties | Test Condition | Test Method | VERSALIS ITALY/CH D0 |
---|---|---|---|
coefficient of friction | 与自身-动态,铸造薄膜 | ISO 8295 | >0.50 |
optical performance | Test Condition | Test Method | VERSALIS ITALY/CH D0 |
---|---|---|---|
gloss | 45°,CastFilm | ASTM D2457 | 80 |
Haze ratio | 铸造薄膜 | ISO 14782 | 4.0 % |
physical property | Test Condition | Test Method | VERSALIS ITALY/CH D0 |
---|---|---|---|
density | ISO 1183 | 0.900 g/cm³ | |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.0 g/10min |
Thermal performance | Test Condition | Test Method | VERSALIS ITALY/CH D0 |
---|---|---|---|
melting temperature | 内部方法 | 115 °C | |
brittle temperature | ASTM D746 | <-70.0 °C | |
vicat | ISO 306/A | 55.0 °C |