Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC S-2000F MITSUBISHI GAS SHANGHAI
IUPILON™ 
Electronic and electrical、Automotive Applications
Medium viscosity、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-2000F
Impact strength of simply supported beam without notch23°CISO179无断裂
Charpy Notched Impact Strength23°CISO17976 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-2000F
Nominal tensile fracture strainISO527-2110 %
Tensile stress屈服ISO527-261.0 Mpa
Tensile strain屈服ISO527-25.6 %
Bending stressISO17893.0 Mpa
Tensile modulusISO527-22400 Mpa
Flexural modulusISO1782300 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-2000F
Surface ResistivityIEC600936E+15 ohms
Relative Permittivity100HzIEC602503.10
Dissipation Factor1MHzIEC602509E-03
dielectric strength1.00mmIEC60243-131 KV/mm
Compared to the Leakage Tracking Index (CTI)CTIUL746PLC 2
Volume resistivityIEC600933E+16 ohms·cm
dielectric strength3.00mmIEC60243-118 KV/mm
Dissipation Factor100HzIEC602506E-04
Relative Permittivity1MHzIEC602503.10
physical property Test ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-2000F
Shrinkage rateTD:3.20mm0.50到0.70 %
Water absorption rate饱和,23°CISO620.24 %
Melt volume flow rate300°C/1.2kgISO11339.00 cm3/10min
Shrinkage rateMD:3.20mm0.50到0.70 %
densityISO11831.20 g/cm³
melt mass-flow rate300°C/1.2kgISO113310 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/S-2000F
1.8MPa, Not annealedISO75-2/A129 °C
Linear thermal expansion coefficientMDISO11359-26.5E-05 cm/cm/°C
0.45MPa, Not annealedISO75-2/B143 °C
Linear thermal expansion coefficientTDISO11359-26.6E-05 cm/cm/°C