PC MB4303 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Automotive components,Electronic and electrical components
Aging resistance,wear resistant
TDS
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB4303 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB4303 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 96 % | |
| bending strength | ISO 178 | 96.0 Mpa | |
| Flexural modulus | ISO 178 | 2400 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.5 % |
| tensile strength | 屈服 | ISO 527-2 | 62.0 Mpa |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB4303 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.50-0.70 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 19.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| Shrinkage rate | MD:3.20mm | 0.50-0.70 % | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/MB4303 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 115 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 97.0 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.8E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.8E-05 cm/cm/°C |