Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HIPS PH-888H TAIWAN CHIMEI
POLYREX® 
Electrical field、Electronic field、Office supplies
heat-resisting
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTAIWAN CHIMEI/PH-888H
Charpy Notched Impact Strength23°CISO 1799.0 kJ/m²
Impact strength of cantilever beam gap23°C,3.20mmASTM D25697 J/m
23°C,6.40mmASTM D25683 J/m
Charpy Notched Impact Strength-30°CISO 1795.2 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A4.5 kJ/m²
23°CISO 180/1A8.0 kJ/m²
hardnessTest ConditionTest MethodTAIWAN CHIMEI/PH-888H
Rockwell hardnessL计秤ASTM D78563
Mechanical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PH-888H
tensile strength 屈服ISO 527-2/5030.0 Mpa
elongation断裂4ASTM D63845 %
bending strength--5ASTM D79044.1 Mpa
--6ISO 17839.0 Mpa
elongation断裂ISO 527-2/5050 %
tensile strength 断裂4ASTM D63829.4 Mpa
Flexural modulus--6ISO 1781500 Mpa
--5ASTM D7901930 Mpa
tensile strength 断裂ISO 527-2/5030.0 Mpa
flammabilityTest ConditionTest MethodTAIWAN CHIMEI/PH-888H
UL flame retardant rating1.5mmUL 94HB
physical property Test ConditionTest MethodTAIWAN CHIMEI/PH-888H
density23°CISO 11831.05 g/cm³
melt mass-flow rate200°C/5.0kgASTM D12383.8 g/10min
Shrinkage rateISO 294-40.40-0.70 %
density--3ASTM D7921.05 g/cm³
Melt volume flow rate200°C/5.0kgISO 11333.80 cm3/10min
Thermal performanceTest ConditionTest MethodTAIWAN CHIMEI/PH-888H
Heat distortion temperature1.8MPa,未退火，HDTASTM D64882.0 °C
1.8MPa,退火，HDTASTM D64897.0 °C
1.8MPa,退火，HDTISO 75-2/A96.0 °C
1.8MPa,未退火，HDTISO 75-2/A79.0 °C
vicat--ASTMD15257102 °C
--ISO 306/B5092.0 °C
Linear coefficient of thermal expansionMDISO 11359-24.0E-5到6.0E-5 cm/cm/°C