PA66 100 W Chem Polymer Company
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Chem Polymer Company/ 100 W |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 64 J/m |
| Mechanical properties | Test Condition | Test Method | Chem Polymer Company/ 100 W |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 7.0 % |
| tensile strength | ASTM D638 | 93.1 MPa | |
| elongation | 屈服 | ASTM D638 | 4.5 % |
| Flexural modulus | ASTM D790 | 3100 MPa | |
| bending strength | ASTM D790 | 117 MPa |
| Electrical performance | Test Condition | Test Method | Chem Polymer Company/ 100 W |
|---|---|---|---|
| dielectric strength | 3.00mm | ASTM D149 | 17 kV/mm |
| Volume resistivity | ASTM D257 | 1E+18 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | Chem Polymer Company/ 100 W |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-2 |
| FMVSS flammability | FMVSS302 | PASSES | |
| Limiting Oxygen Index | ASTM D2863 | 28 % |
| physical property | Test Condition | Test Method | Chem Polymer Company/ 100 W |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 1.2to1.8 % |
| density | ASTM D792 | 1.16 g/cm³ |
| Thermal performance | Test Condition | Test Method | Chem Polymer Company/ 100 W |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 107 °C |
| melting temperature | DSC | 257 °C |