PA CM3501G50 TORAY JAPAN
--
--
Filler, glass fiber reinforced material, 50%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/ CM3501G50 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 23 kJ/m² |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/ CM3501G50 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 14200 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.2 % |
| tensile strength | 23°C | ISO 527-2 | 205 MPa |
| bending strength | 23°C | ISO 178 | 315 MPa |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/ CM3501G50 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1.0E+12到1.0E+13 ohms·cm |
| flammability | Test Condition | Test Method | TORAY JAPAN/ CM3501G50 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/ CM3501G50 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.59 g/cm³ |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.50to0.70 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
| Shrinkage rate | MD:3.00mm3 | 内部方法 | 0.20to0.40 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/ CM3501G50 |
|---|---|---|---|
| thermal conductivity | 0.40 W/m/K | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 223 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.0E-5到3.0E-5 cm/cm/°C |
| melting temperature | DSC | 228 °C | |
| specific heat | 1500 J/kg/°C |