Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 310-7002 SABIC INNOVATIVE JAPAN
VALOX™
Electrical applications、Automotive Applications、currency
High rigidity、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310-7002 |
|---|---|---|---|
| Dart impact | 23°C6 | ASTM D3029 | 40.7 J |
| 23°C | ASTM D3029 | 40.7 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310-7002 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 117 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310-7002 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 300 % |
| tensile strength | Break | ASTM D638 | 51.7 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 82.7 Mpa |
| Break,50.0mmSpan | ASTM D790 | 82.7 Mpa | |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 2340 Mpa |
| tensile strength | 屈服 | ASTM D638 | 51.7 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310-7002 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| Volume resistivity | ASTM D257 | >4.0E+16 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.020 |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 23 KV/mm |
| 3.20mm,在油中 | ASTM D149 | 16 KV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 3.10 |
| arc resistance | ASTM D495 | PLC 5 | |
| dielectric constant | 100Hz | ASTM D150 | 3.30 |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 16 KV/mm |
| 1.60mm,在油中 | ASTM D149 | 23 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310-7002 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310-7002 |
|---|---|---|---|
| Shrinkage rate | TD：--2 | 内部方法 | 1.0-1.7 % |
| TD：--3 | 内部方法 | 1.6-2.4 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.080 % |
| Shrinkage rate | MD：--2 | 内部方法 | 0.90-1.6 % |
| Specific volume | ASTM D792 | 0.770 cm³/g | |
| Shrinkage rate | MD：--3 | 内部方法 | 1.5-2.3 % |
| melt viscosity | 内部方法 | 600 Pa·s |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310-7002 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 54.4 °C |
| Linear coefficient of thermal expansion | MD：60to138°C | ASTME831 | 1.4E-04 cm/cm/°C |
| MD：-40to40°C | ASTME831 | 8.1E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 154 °C |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 140 °C | |
| RTI Elec | UL 746 | 120 °C |