PA66 A3X2G10 BK BASF MALAYSIA
Ultramid®
Laptop case、Industrial machinery
High mobility、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF MALAYSIA/A3X2G10 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 / 16 kJ/m² |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eA | 55 / 55 kJ/m² |
| -30℃ | ISO 179/1eA | 50 / - kJ/m² | |
| Charpy Notched Impact Strength | -30℃ | ISO 179/1eA | 11 / - kJ/m² |
| Impact strength of cantilever beam gap | 23℃ | ISO 180-A | 14 / 20 kJ/m² |
| Flammable | Test Condition | Test Method | BASF MALAYSIA/A3X2G10 BK |
|---|---|---|---|
| Glow wire combustion index (GWFI) | 厚度10mm | IEC 60695-2-12 | 960 °C |
| smoke toxicity | NF X70-100-1/-2 | 0.36 | |
| Smoke density | EN ISO 5659-2: 2007 | 184 | |
| Limiting Oxygen Index | ISO 4589-1/-2 | 27 % |
| Electrical performance | Test Condition | Test Method | BASF MALAYSIA/A3X2G10 BK |
|---|---|---|---|
| Volume resistivity | 表面电阻率 | IEC 60112 | 600 ohms |
| IEC 60093 | /1E10 Ohm*m | ||
| dielectric constant | 1MHz | IEC 60250 | 3.6 / 5 |
| Dissipation Factor | IEC 60093 | 1E13 / 1E10 E-4 |
| Mechanical properties | Test Condition | Test Method | BASF MALAYSIA/A3X2G10 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-1-2 | 16000 / 12000 Mpa | |
| Tensile strain | ISO 527-1-2 | 180 / 130 Mpa | |
| Flexural modulus | ISO 178 | 13000 / - Mpa | |
| Tensile creep modulus | 1000小时，应变<= 0.5％，23℃ | ISO 899-1 | * / 5400 Mpa |
| handle | Test Condition | Test Method | BASF MALAYSIA/A3X2G10 BK |
|---|---|---|---|
| melting temperature | ISO 11357-1/-3 | 260 °C | |
| Melt Temperature | 290 - 300 °C | ||
| Temperature | 80-90 °C |
| physical property | Test Condition | Test Method | BASF MALAYSIA/A3X2G10 BK |
|---|---|---|---|
| Water absorption rate | 平衡，23℃，50% RH，2.00 mm | ISO 62 | 0.70 - 1.10 % |
| 饱和 | ISO 62 | 3.7 - 4.3 % | |
| density | ISO 1183 | 1.6 g/cm³ | |
| Shrinkage rate | TD | 0.4 % | |
| Viscosity value | 0.5% in 96 % H2SO4 | ISO 307 | 140 cm³/g |
| Melt volume flow rate | 275℃，5 kg | ISO 1133 | 25 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF MALAYSIA/A3X2G10 BK |
|---|---|---|---|
| Linear coefficient of thermal expansion | 横向：23~80°C | ISO 11359-1/-2 | 40-50 E-6/K |
| MD：23~80℃ | ISO 11359-1/-2 | 15 - 20 E-6/K | |
| Heat distortion temperature | 1.8 MPa，HDT | ISO 75-1/2 | 250 °C |
| 0.45 MPa，HDT | ISO 75-1/2 | 250 °C |