Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 551G JILIN JOINATURE
ZYPEEK®
Medical supplies、Nursing supplies
Moderate liquidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JILIN JOINATURE/551G |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180-A | 6.5 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179/1eA | 6 kJ/m² |
| Mechanical properties | Test Condition | Test Method | JILIN JOINATURE/551G |
|---|---|---|---|
| tensile strength | 屈服，23℃ | ISO 527 | 100 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 4200 Mpa |
| compressive strength | 23℃ | ISO 604 | 125 Mpa |
| bending strength | 屈服，23℃ | ISO 178 | 170 Mpa |
| Shore hardness | 23℃ | ISO 868 | 85 D 级 |
| Tensile strain | 断裂，23℃ | ISO 527 | 40 % |
| Electrical performance | Test Condition | Test Method | JILIN JOINATURE/551G |
|---|---|---|---|
| dielectric strength | 2 mm | IEC 60243-1 | 23 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| Loss factor | 23℃, 1MHz，正切 | IEC 60250 | 0.003 |
| dielectric constant | 23 ℃, 1 kHz | IEC 60250 | 3.2 |
| 23 ℃, 50 Hz | IEC 60250 | 4.5 | |
| Volume resistivity | 23 ℃，1V | IEC 60093 | 10^16 ohms·cm |
| 275 ℃ | IEC 60093 | 10^9 ohms·cm |
| physical property | Test Condition | Test Method | JILIN JOINATURE/551G |
|---|---|---|---|
| density | 结晶 | ISO 1183 | 1.3 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 1 % |
| MD | ISO 294-4 | 1.3 % | |
| Water absorption rate | 23℃，24hr，3.2 mm厚拉伸棒 | ISO 62-1 | 0.07 % |
| 平衡，23℃，3.20 mm厚拉伸棒 | ISO 62-1 | 0.4 % | |
| melt mass-flow rate | 380℃，5.0kg | ISO 1133 | 14 g/10min |
| density | 非结晶 | ISO 1183 | 1.26 g/cm³ |
| Thermal performance | Test Condition | Test Method | JILIN JOINATURE/551G |
|---|---|---|---|
| Heat distortion temperature | 1.8 Mpa，HDT | ISO 75-f | 152 °C |
| Linear coefficient of thermal expansion | 低于Tg沿着流动方向 | ISO 11359 | 45 ppm/K |
| Glass Transition Temperature | 起始 | ISO 11357 | 143 °C |
| melting temperature | ISO 11357 | 343 °C | |
| thermal conductivity | 23℃ | ISO 22007-4 | 0.29 W/m/K |
| specific heat | 23℃ | DSC | 2.2 kJ/kg/℃ |
| Linear coefficient of thermal expansion | 高于Tg沿着流动方向 | ISO 11359 | 120 ppm/K |