NBR NANCAR® 1041 Nantex Industry Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Nantex Industry Co., Ltd./NANCAR® 1041 |
|---|---|---|---|
| Shore hardness | 邵氏A,5秒5 | ASTM D2240 | 75 |
| 邵氏A,5秒3 | ASTM D2240 | 73 | |
| 邵氏A,5秒4 | ASTM D2240 | 74 |
| elastomer | Test Condition | Test Method | Nantex Industry Co., Ltd./NANCAR® 1041 |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D412 | 27.3 MPa |
| 屈服5 | ASTM D412 | 26.6 MPa | |
| 屈服3 | ASTM D412 | 28.0 MPa | |
| 300%应变4 | ASTM D412 | 12.7 MPa | |
| 300%应变3 | ASTM D412 | 11.3 MPa | |
| compression set | 100°C,70hr | ASTM D395 | 59 % |
| tensile strength | 300%应变5 | ASTM D412 | 13.9 MPa |
| elongation | 断裂5 | ASTM D412 | 500 % |
| 断裂4 | ASTM D412 | 550 % | |
| 断裂3 | ASTM D412 | 600 % | |
| tear strength | ASTM D624 | 61.0 kN/m |
| aging | Test Condition | Test Method | Nantex Industry Co., Ltd./NANCAR® 1041 |
|---|---|---|---|
| Change rate of hardness (Shore) in the air | 支撐A,100°C,70hr,在IRM903油中 | ASTM D471 | -6.0 |
| Change rate of ultimate elongation in air | 100°C,70hr,在ASTM#1油中 | ASTM D471 | -26 % |
| Change rate of hardness (Shore) in the air | 支撐A,100°C,70hr,在ASTM#1油中 | ASTM D471 | 2.0 |
| Change rate of ultimate elongation in air | 100°C,70hr | ASTM D573 | -29 % |
| Change rate of tensile strength in air | 100°C,70hr,在ASTM#1油中 | ASTM D471 | -6.0 % |
| volume change | 100°C,70hr,ASTM标准油（1号） | ASTM D471 | -0.90 % |
| Change rate of tensile strength in air | 100°C,70hr | ASTM D573 | -8.0 % |
| 100°C,70hr,在IRM903油中 | ASTM D471 | -11 % | |
| volume change | 100°C,70hr,在IRM903油中 | ASTM D471 | 10 % |
| Change rate of ultimate elongation in air | 100°C,70hr,在IRM903油中 | ASTM D471 | -19 % |
| Change rate of hardness (Shore) in the air | 邵氏A,100°C,70hr | ASTM D573 | 3.0 |
| physical property | Test Condition | Test Method | Nantex Industry Co., Ltd./NANCAR® 1041 |
|---|---|---|---|
| density | 1.00 g/cm³ | ||
| Soluble inMEK | 100 % | ||
| bound acrylonitrile content | 内部方法 | 41.0 % | |
| Viscosity | Minimum | ASTM D1646 | 56.0 |
| Mooney viscosity | ML1+4,100°C | ASTM D1646 | 82 MU |
| Viscosity | Minutesto35pointsrise,t35 | ASTM D1646 | 35.7 min |
| Mooney viscosity | ML1+4,100°C2 | ASTM D1646 | 100 MU |
| Viscosity | Minutesto5pointsrise,t5 | ASTM D1646 | 33.3 min |
| stabilizer | Non-staining |
| Thermal performance | Test Condition | Test Method | Nantex Industry Co., Ltd./NANCAR® 1041 |
|---|---|---|---|
| Heat loss | ASTM D5688 | 0.40 % |