Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DX06313 GY7E079L SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electrical enclosure、Thin walled components
High mobility、enhance、High impact resistance、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX06313 GY7E079L |
|---|---|---|---|
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 136 °C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831,ISO11359-2 | 2.2E-05 cm/cm/°C |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 136 °C | |
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831,ISO11359-2 | 6.8E-05 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX06313 GY7E079L |
|---|---|---|---|
| Break | ASTMD638 | 99.0 Mpa | |
| fracture | ISO527-2/5 | 90.0 Mpa | |
| ASTMD638 | 7500 Mpa | ||
| Break | ASTMD638 | 3.6 % | |
| Yield,50.0mm Span | ASTMD790 | 170 Mpa | |
| 50.0mm Span | ASTMD790 | 7000 Mpa | |
| fracture | ISO527-2/5 | 3.5 % | |
| ISO178 | 170 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/DX06313 GY7E079L |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.10 % |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 32.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.30到0.50 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 4.6 g/10min |
| 300°C/5.0kg | ASTMD1238 | 42 g/10min | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.40 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/DX06313 GY7E079L |
|---|---|---|---|
| ASTMD256 | 190 J/m | ||
| ISO180/1A | 17 kJ/m² | ||
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 24.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 16 kJ/m² |